Anti-blue light and hydrophobic composite film based on iron oxide and FAS-modified SiO 2

Jianhua Zhang,Jiaqi Yu,Xingyang Wu,Weidong Qiao,Hongdong Wang

DOI: https://doi.org/10.1016/j.apsusc.2024.160449

IF: 6.7

2024-06-05

Applied Surface Science

Abstract:With the increasing application of display and lighting devices, the potential injury to human eyes due to blue light has been attracting significant attention. While current anti-blue light films are complex, costly and low stability in humid environments. In this work, anti-blue light films were fabricated using iron oxide as blue light absorbent and polyvinylpyrrolidone as surfactant, under various Fe 3+ concentrations and annealing temperatures. Particularly, the films annealed at 300 °C exhibited 60 % absorption rate of blue light in 400–450 nm wavelength range on average and still maintained 96 % transmittance to 500–800 nm visible light. Moreover, the films coated with 1H,1H,2H,2H-perfluorodecyltriethoxysilane (FAS)-modified SiO 2 hydrophobic layer showed high hydrophobicity and sequential humid-heat stability. Meanwhile, no obvious changes occurred in transmittance spectra after keeping at 85 °C and 85 % relative humidity for 15 days. With the composite film covered, the color rendering index of the display screen decreased only 0.7 %, while the blue light weighted radiance decreased significantly by 37.1 %. Furthermore, cell experiments with composite films demonstrated that human retinal pigment epithelium cells were effectively protected from blue light injury. Overall, the composite films with high stability exhibited desired anti-blue light function.

materials science, coatings & films,physics, applied,chemistry, physical, condensed matter