First Principles Density Functional Theory Study of Tritium Species Adsorption on Ni(111) Surface and Diffusion in Nickel-sublayer for Tritium Storage

De Nyago Tafen,Hari Paudel,Andrew Casella,David Senor,Yuhua Duan

DOI: https://doi.org/10.1039/d4cp04398g

IF: 3.3

2024-12-06

Physical Chemistry Chemical Physics

Abstract:The nickel-plated zircaloy-4 is used as a tritium ( 3 H) getter in the tritium-producing burnable absorber rods (TPBARs) to capture 3 H produced in the 6 Li-riched annular γ-LiAlO 2 pellet under neutron irradiation. The experimental data and our previous theoretical results showed that the 3 H species produced from the γ-LiAlO 2 pellet were mainly 3 H 2 and 3 H 2 O. These 3 H species diffuse from the surface of the LiAlO 2 pellet across vacuum to the nickel-plated zircaloy-4 getter and then further diffuse into the getter to chemically form metal hydrides. While a number of studies show that oxygen binds strongly as compared to 3 H on the nickel (Ni) layer, the detailed mechanism of 3 H species absorption and diffusion across the Ni plate and Ni/Zr interface are still unclear. By employing density functional theory calculations, here we explored the 3 H 2 and 3 H 2 O species adsorption and dissociation on the Ni (111) surface and diffusion into the Ni sublayer. Our results indicate that the 3 H 2 and 3 H 2 O dissociate on the Ni (111) surface. The NiO x and Ni(O 3 H) x could be formed in the Ni layer due to the higher oxygen (O) diffusion energy barrier and formation of Ni vacancy defects. The oxygen was found to be retained in the Ni layer from diffusing across the Ni-Zr interface. This was revealed by comparing the diffusion barriers for 3 H with O. 3 H was found to have nearly three times smaller diffusion barrier than for O, making 3 H comparatively easier to diffuse through the Ni layer. The obtained results provide guidelines for experimental measurements on 3 H retention behavior in TPBARs and may open further avenues to explore the impurity effects on 3 H diffusion and storage at the Ni/Zircaloy interfaces.

chemistry, physical,physics, atomic, molecular & chemical