Abstract:Harnessing two-dimensional (2D) materials for catalytic applications is promising due to the high site utilization. Here, we synthesized a 2D molybdenum carbonitride of the MXene family, Mo2(C,N)Tx, and applied it as a catalyst for ammonia synthesis and decomposition, the essential reactions to establish NH3 as an energy vector. We determine the thermal stability limit of Mo2(C,N)Tx under H2 flow to be ca. 575 C. Exceeding this temperature results, under H2, in a transformation of the predominantly defunctionalized Mo2(C,N)Tx to a 3D Mo2(C,N) phase, which prevents the complete defunctionalization of Mo2(C,N)Tx while retaining its 2D morphology. Before this phase transformation occurs, the remaining Tx species reside in the interior layers of the mostly defunctionalized Mo2(C,N)Tx nanoplatelets, with the exterior being free from Tx groups, rendering the Mo2(C,N)Tx nanoplatelets chemically anisotropic in the direction orthogonal to the basal plane. The effect of this structure on catalytic properties is highlighted in the thermocatalytic synthesis and decomposition of NH3. In the latter reaction, Mo2(C,N)Tx shows similar gravimetric rates to a reference bulk β-Μο2Ν catalyst, which is ascribed to the presence of too narrow 2D pores (ca. 5.2 Å) with irregular shapes due to a disorder in the stacking of nanosheets in Mo2(C,N)Tx, limiting interlayer diffusion. A deactivation pathway in Mo-based MXenes was identified and it relates to a precipitation of carbon vacancies to metallic molybdenum under NH3 decomposition conditions. While the ammonia decomposition reaction shows no dependence of the reaction rate on the specific H2 pretreatment of Mo2(C,N)Tx (500 or 575 C), the gravimetric ammonia formation rate increases appreciably with H2 pretreatment, viz., Mo2(C,N)Tx pretreated at 575 C outperforms by ca. four times both the reference β-Μο2Ν catalyst and Mo2(C,N)Tx pretreated at 500 C, explained by a smaller molecule size of the reactants H2 and N2 relative to NH3, and an increased accessibility and utilization of the interlayer space for ammonia synthesis. Overall, our study highlights the importance of addressing limitations due to small pore sizes in multilayered MXenes and the stability of carbon vacancies while simultaneously using optimized pretreatment conditions for surface defunctionalization to uncover the full potential of MXene-based heterogeneous catalysts.

Unlocking the Potential of MXene in Catalysis: Decorated Mo 2 CT x Catalyst for Ammonia Synthesis under Mild Conditions

Efficient Electrocatalytic N2 Fixation with MXene under Ambient Conditions

Multilayered Molybdenum Carbonitride MXene: Reductive Defunctionalization, Thermal Stability, and Catalysis of Ammonia Synthesis and Decomposition

Enhanced Photofixation of Dinitrogen to Ammonia over a Biomimetic Metal (Fe,Mo)-Doped Mesoporous MCM-41 Zeolite Catalyst under Ambient Conditions

An MnO2-Ti3C2Tx MXene Nanohybrid: an Efficient and Durable Electrocatalyst Toward Artificial N-2 Fixation to NH3 under Ambient Conditions

Surface Oxidation of Ti3C2Tx Enhances the Catalytic Activity of Supported Platinum Nanoparticles in Ammonia Borane Hydrolysis

Perspectives on Electrochemical Nitrogen Fixation Catalyzed by Two-Dimensional MXenes

Novel confinement of Mn3O4 nanoparticles on two-dimensional carbide enabling high-performance electrochemical synthesis of ammonia under ambient conditions

NH3 Synthesis Via Electrocatalytic N2 Reduction Reaction on the Defective Surfaces of Nb2Mo2C3Tx MXenes: Theoretical and Experimental Studies

Amorphous CoMoO4 with Nanoporous Structures for Electrochemical Ammonia Synthesis under Ambient Conditions

Cu-based MOF-derivatived catalyst for efficient electrocatalytic reduction of nitrogen and nitrate to produce ammonia

MoO3 Nanosheets for Efficient Electrocatalytic N2 Fixation to NH3

Controllable Exfoliation of MOF‐Derived Van Der Waals Superstructure into Ultrathin 2D B/N Co‐Doped Porous Carbon Nanosheets: A Superior Catalyst for Ambient Ammonia Electrosynthesis

Spatial confinement and electron transfer moderating Mo N bond strength for superior ammonia decomposition catalysis

Single platinum atoms immobilized on an MXene as an efficient catalyst for the hydrogen evolution reaction

A Graphene Oxide‐supported PdCu Catalyst for Enhanced Electrochemical Synthesis of Ammonia

Mn 3 O 4 Nanocube: An Efficient Electrocatalyst Toward Artificial N 2 Fixation to NH 3 .

Synergistic N/F Dual-Doped MoC/C Catalyst Synthesized via Liquid Phase Plasma for Sustainable Ammonia Production

Unveiling the key intermediates in electrocatalytic synthesis of urea with CO2 and N2 coupling reactions on double transition-metal MXenes

Molybdenum Carbide Nanodots Enable Efficient Electrocatalytic Nitrogen Fixation under Ambient Conditions

Amorphous CoMoO 4 with Nanoporous Structures for Electrochemical Ammonia Synthesis under Ambient Conditions