Abstract:In order to understand the effect of precipitation on the slip activities of Mg-Gd-Y-Zn-Zr alloys, the dislocation slip activities of solid-solution and as-aged alloys during ambient temperature quasi-in-situ compression were quantitatively investigated by electron backscattered diffraction (EBSD)-assisted slip trace analysis. First, slip trace analysis of both alloys showed that the β' precipitates reduced the frequency and number of grains with slip traces significantly, resulting in a pronounced precipitate-hardening behavior. At 11% strain, the aging treatment reduced the proportion of prismatic slip and second-order pyramidal slip by 4.6% and 9.3%, respectively, while the proportion of basal slip increased by 13.9%, indicating that the precipitate-hardening effect of non-basal slip was stronger than that of basal slip. Moreover, based on the slip trace statistical analysis and TEM images of the sheared β' precipitates, the critical resolved shear stress (CRSS) increments of different slip modes caused by the prismatic plate-shaped β' precipitates follow the order of Δτpyramidal-2 > Δτprismatic > Δτbasal. Also, we found the plastic inhomogeneity of solid-solution alloy during ambient temperature deformation can increase the propensity of non-basal dislocation slip and promote non-Schmid behaviors. However, a large number of fine β' precipitates dispersed in the as-aged alloy can effectively alleviate the plastic inhomogeneity in the grain-scale range during ambient temperature deformation. Further, TEM dislocation analysis under two-beam conditions shows that the abundant solute RE atoms in the solid-solution Mg-Gd-Y-Zn-Zr alloy contribute to the activity of second-order pyramidal dislocations. Therefore, we conclude that the changes in slip activity caused by the precipitation of Mg-Gd-Y-Zn-Zr alloys are mainly attributed to β' precipitates, plastic inhomogeneity, and solute RE atoms.

Activation of dislocations in Mg with solute Y

Local Lattice Distortion Mediated Formation of Stacking Faults in Mg Alloys

Origins and dissociation of pyramidal <c + a> dislocations in magnesium and its alloys

Enhancing the strain hardening and ductility of Mg-Y alloy by introducing stacking faults

Deformation mechanisms of basal slip, twinning and non-basal slips in Mg–Y alloy by micropillar compression

Solute softening and vacancy generation by diffusion-less climb in magnesium alloys

A comprehensive theoretical scheme for understanding the core structure and the mechanical behavior of basal dislocations with solute atmosphere in Mg alloys

Role of micro-alloying element in dynamic deformation of Mg-Y alloys

Localized dislocation interactions within slip bands and crack initiation in Mg-10Gd-3Y-0.3Zr alloy

Role of Y on the microstructure and mechanical properties of Mg-Gd-Zr alloy

Simulation on Microstructure Evolution and Mechanical Properties of Mg−Y Alloys: Effect of Trace Y

Solute effect on basal and prismatic slip systems of Mg

Comparative study on dislocation slip activity of the solid-solution and as-aged Mg-9.8Gd-3.5Y-2.0Zn-0.4Zr (wt%) alloys during ambient temperature quasi-in-situ compression

Role of prismatic dislocations in sub-zero temperature deformation of Mg-Gd-Y-Zr alloy

Solute atom mediated Hall-Petch relations for magnesium binary alloys

Unveiling precipitation behavior in Mg-Y based alloys

Critical resolved shear stresses for slip and twinning in Mg-Y-Ca alloys and their effect on the ductility

Microstructures, hot tensile deformation behavior and constitutive modeling in a superlight Mg-2.76Li-3Al-2.6Zn-0.39Y alloy

Enhanced strength-ductility synergy and activation of non-basal slip in as-extruded Mg–Zn–Ca alloy via heterostructure

Dislocation-induced Y segregation at basal-prismatic interfaces in Mg

Enhanced superplasticity achieved by disclination-dislocation reactions in a fine-grained low-alloyed magnesium system