Grain orientations and failures mechanism of isothermal aged nano Sn-3Ag-0.5Cu/Cu solder joints by microwave hybrid heating and sheer mechanical strength
Shuai Zhang,Hongzhi Zhou,Tianran Ding,Weimin Long,Sujuan Zhong,Kyung-Wook Paik,Peng He,Shuye Zhang
DOI: https://doi.org/10.1016/j.engfracmech.2024.109902
IF: 5.4
2024-02-04
Engineering Fracture Mechanics
Abstract:The application of microwave hybrid heating (MHH) technique in low-temperature joining presents a notable benefit of delivering both selective and uniform heating, a characteristic that is not typically found in traditional welding techniques. This experimental investigation aimed to evaluate the reliability of joints under a uniform temperature condition compared to those formed through the reflow soldering method. The present study successfully achieved joint formation through the utilization of the reflow soldering technique, utilizing a maximum temperature of 250 °C and a reflow time of 600 s. EBSD characterization , revealed the occurrence of recovery and recrystallization at the joint. Moreover, as the duration of aging increases, the crystallographic orientation of Sn and Cu 6 Sn 5 becomes more prominent, with Cu 6 Sn 5 exhibiting growth predominantly along a specific direction [0 0 1]. In addition, the MHH technique was employed, using specific parameters of 900 W and 195 s, to achieve successful joint production. Empirical findings revealed that reflow joints saw a significant drop of 34.2 % in their shear strength after being aged for 7 days. Likewise, the shear strength of MHH joints decreased by 28.9 % under the same aging conditions. During the aging process spanning 21–28 days, the decrease in shear strength proportion gradually diminishes. More precisely, the reflow soldering head experiences a reduction of merely 7.6 %, while MHH demonstrates a decrease of only 2.5 %. The joint's fracture pattern shifted from primarily ductile to a combination of mixed fracture after a duration of 28 days for both soldering methods, which contrasts with the previously observed timeframe of 7–21 days.
mechanics