Enhancing the Gas Separation Selectivity of Mixed-Matrix Membranes Using a Dual-Interfacial Engineering Approach

Chunhui Wu,Kexin Zhang,Hongliang Wang,Yaqi Fan,Songwei Zhang,Sanfeng He,Fang Wang,Yu Tao,Xiaowen Zhao,Yue-Biao Zhang,Yanhang Ma,Yongjin Lee,Tao Li
DOI: https://doi.org/10.1021/jacs.0c07378
IF: 15
2020-10-14
Journal of the American Chemical Society
Abstract:We report a dual-interfacial engineering approach that uses a sub-20 nm polycrystalline MOF-74 shell as a transition phase to engineer the MOF–polymer interface. The application of a shell MOF layer divides the original single interface problem into two interfaces: MOF–MOF and MOF–polymer, which can be individually addressed. The greater external surface area created by the uneven MOF-74 shell containing high-density open metal sites allows the MOF to interact with 300% polymer at the interface compared to traditional MOF, thereby ensuring good interfacial compatibility. When applied on UiO-66-NH<sub>2</sub>, its respective mixed-matrix membranes exhibit a simultaneous increase of CO<sub>2</sub>/CH<sub>4</sub> separation selectivity and CO<sub>2</sub> permeability with increasing MOF loading, implying a defect-free interface. When applied on MOF-801, the mixed-matrix membranes exhibit an ethylene/ethane separation selectivity up to 5.91, a drastic 76% increase compared to that of the neat polymer owing to a "gas focusing" mechanism promoted by the preferred pore orientation in the MOF-74 layer. This represents one of the most selective ethylene/ethane separation membranes reported to date.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/jacs.0c07378?goto=supporting-info">https://pubs.acs.org/doi/10.1021/jacs.0c07378</a>.Materials, synthesis, characterization, supplemental figures and tables, and references (<a class="ext-link" href="/doi/suppl/10.1021/jacs.0c07378/suppl_file/ja0c07378_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to enhance the gas separation selectivity of mixed - matrix membranes (MMMs) through a dual - interface engineering method. Specifically, the researchers developed a method to engineer the MOF - polymer interface using a sub - 20 - nm polycrystalline MOF - 74 shell as a transition phase. This method can decompose the original single - interface problem into two independent interface problems: the MOF - MOF interface and the MOF - polymer interface, so that they can be optimized separately. ### Main problems and objectives 1. **Improve gas separation performance**: By improving the compatibility of the MOF - polymer interface, increase the separation selectivity and permeability of CO₂/CH₄ and C₂H₄/C₂H₆. 2. **Solve interface defects**: The traditional MOF - polymer interface has problems of weak interaction and small contact area, resulting in interface defects and affecting the separation performance. The method proposed in this paper aims to solve these problems by increasing the external surface area and improving the interface interaction. 3. **Achieve high selectivity and high permeability**: By introducing specific structural features (such as open metal sites and preferred pore orientations) in the MOF - 801 and MOF - 74 layers, the goal of simultaneously increasing selectivity and permeability is achieved. ### Key innovation points 1. **Dual - interface engineering method**: By growing a thin polycrystalline MOF - 74 shell on the surface of the MOF core, the single - interface problem is decomposed into two independent interface problems for separate optimization. 2. **Increase surface area and interaction**: The uneven surface of the polycrystalline MOF - 74 shell increases the external surface area, increasing the interaction area between the MOF and the polymer by more than 300%, thereby improving the interface compatibility. 3. **Gas - focusing mechanism**: The 1 - D pores in the MOF - 74 layer are perpendicular to the surface of MOF - 801, promoting the vertical transport of gas molecules and hindering the horizontal diffusion, thereby enhancing the selective separation of C₂H₄/C₂H₆. ### Experimental results - **CO₂/CH₄ separation**: The mixed - matrix membrane using the MOF - 74 layer simultaneously increased the separation selectivity of CO₂/CH₄ and the permeability of CO₂ when the MOF loading was increased, indicating that the interface was defect - free. - **C₂H₄/C₂H₆ separation**: For the mixed - matrix membrane using MOF - 801 and MOF - 74 layers, the selectivity of C₂H₄/C₂H₆ reached a maximum of 5.91, which was 76% higher than that of the pure polymer membrane and was one of the most efficient C₂H₄/C₂H₆ separation membranes reported so far. ### Conclusion This paper successfully improved the gas separation performance of mixed - matrix membranes through the dual - interface engineering method, especially made significant progress in C₂H₄/C₂H₆ separation. This method not only solves the problems existing in the traditional MOF - polymer interface but also provides a general strategy that can be applied to other types of MOF materials, further promoting the development of gas separation technology.