Temperature-dependent mechanical properties of polyetherimide composites reinforced by graphene oxide-coated short carbon fibers

Zheng Sun,Yuan-Qing Li,Pei Huang,Hua-Jun Cao,Wei Zeng,Jia Li,Fei Li,Bao-Gang Sun,Han-Qiao Shi,Zi-li Zhou,Ning Hu,Shao-Yun Fu

DOI: https://doi.org/10.1016/j.compstruct.2021.114075

IF: 6.3

2021-08-01

Composite Structures

Abstract:<p>Graphene oxide (GO) has been well accepted as one novel fiber sizing agent for enhancing the mechanical properties at low temperature or room temperature (RT) of short carbon fiber reinforced polymer composites. But knowledge is still lacking about the mechanical behaviors at elevated temperature of GO-coated short fiber reinforced polymer composites. Here the temperature-dependent tensile properties of GO-sized short carbon fiber () reinforced polyetherimide (PEI) composites were systematically investigated from -70℃ to 170℃. The /PEI composites with varied GO sizing contents were prepared via an efficient injection molding technique. The /PEI composite with 0.4 wt% GO content was shown to be optimal for the tensile strength at RT and thus was selected to investigate temperature-dependent tensile behaviors. The results show that the GO sizing treatment plays a positive role in enhancing the tensile strength of SCF/PEI composites at -70℃ and 30℃ whereas a negative role at 100℃ and 170℃. Morphological observation indicates that the fiber-matrix interface is enhanced at -70℃ and 30℃ but deteriorated at 100℃ and 170℃ due to the thermal expansion mismatch between GO and PEI. In addition, appropriate empirical equations were established for elucidating the relationships between their strength/modulus and temperature of PEI, SCF/PEI and /PEI composites.</p>

mechanics,materials science, composites