Abstract:Liquid-phase epitaxy (LPE) is one of the best techniques for the preparation of single crystal garnet films. However, the specific Faraday rotation angle of Yttrium iron garnet (YIG) is small, and its easy magnetization axis is parallel to the film surface. The YIG requires a large external saturation field, which cannot meet the development needs of magneto-optical devices. It is found that Bi-substituted YIG(Bi:YIG) film has a larger specific Faraday angle. By adjusting the easy magnetization axis of Bi: YIG perpendicular to the film surface, the saturation magnetization of Bi: YIG can be reduced, so that it can work under a small external magnetic field. This meets the development needs of miniaturization and energy saving of magneto-optical device. The saturation magnetization of garnet film can be effectively reduced by substituting Ga3+ for YIG crystal, mainly for Fe3+ at the 24d position of its tetrahedron. And the lattice constants of Gd3Ga5O12 (GGG) and YIG are 1.2383 nm and 1.2376 nm, respectively. However, the radius of Bi3+ (10.8 nm) is larger than that of Y3+ (9.0 nm), the lattice mismatch of garnet film increases with the incorporation of Bi3+. In order to neutralize the lattice expansion caused by Bi3+, Tm3+ (8.69 nm) with a radius smaller than that of Y3+ (9.0 nm) is selected. Based on the theoretical analysis of the magnetocrystalline anisotropy of garnet film, (BiTm)3(GaFe)5O12 mono-crystalline films with different growth temperatures and different thickness values are grown by LPE on GGG (111) substrates. The experimental results show that when the thickness of epitaxial film is greater than 1 μm, the influence of shape anisotropy on magnetocrystalline anisotropy can be ignored. With the increase of growth temperature, the substitution number of Bi3+ ions decreases gradually, the lattice constant of epitaxial film decreases gradually, and the lattice mismatch first decreases and then increases. Then, the state of compressive stress gradually changes into that of tensile stress. Compared with growth-induced anisotropy, the stress-induced anisotropy is dominant in the change of magnetocrystalline anisotropy. The Verdet constant of (BiTm)3(GaFe)5O12 film is 11.8 × 104 rad/Tm@1064 nm. The results show that the prepared (BiTm)3(GaFe)5O12 mono-crystalline films have great development potential in magneto-optical devices.

Revealing Site Occupancy in a Complex Oxide: Terbium Iron Garnet

Strain-Tunable Magnetic Compensation Temperature of Epitaxial Tb$_3$Fe$_5$O$_{12}$ Thin Films

Atomic order of rare earth ions in a complex oxide: a path to magnetotaxial anisotropy

Tunable Compensation Temperature Through Ferromagnetic Coupling in Perpendicular Tb3fe5o12/Eu3fe5o12 Bilayer Heterostructure

Continuous Tuning of Compensated Ferrimagnetism in Gd3–xHoxFe5O12 Thin Films

The thickness effect on the compensation temperature of rare-earth garnet thin films

Sputtered terbium iron garnet films with perpendicular magnetic anisotropy for spintronic applications

Probing exchange bias at the surface of a doped ferrimagnetic insulator

Atomic-Scale Control of Magnetism at the Titanite-Manganite Interfaces.

Interface and Surface Cation Stoichiometry Modified by Oxygen Vacancies in Epitaxial Manganite Films

Interfacial magnetic characteristics of nearly compensated gadolinium iron garnet

Defect Engineering in Epitaxial Thin Films of the Pyrochlore Frustrated Magnet Tb 2 Ti 2 O 7

High Figure of Merit Magneto‐Optical Ce‐ and Bi‐Substituted Terbium Iron Garnet Films Integrated on Si

Temperature‐Dependent Surface Anisotropy in (110) Epitaxial Rare Earth Iron Garnet Films

Atomic-scale insights into quantum-order parameters in bismuth-doped iron garnet

Giant reduced magnetic anisotropy in magneto-optical garnet

First Principles Calculation On The Magnetic, Optical Properties And Oxygen Vacancy Effect Of Cexy3-Xfe5o12

Preparation and Orientation Mechanism Analysis of (bitm)3(gafe)5o12 Magneto-Optical Single Crystal Film with Out-of-plane Orientation

Optimization On Magnetic Transitions And Magnetostriction In Tbxdyyndz(Fe0.9co0.1)(1.93) Compounds

Supplemental Materials for “ Photo-Spin-Voltaic Effect ”

Interfacial Electronic and Magnetic Reconstructions in Manganite/Titanate Superlattices