Effective density and packing of compacted soot aggregates

Timothy A. Sipkens,Joel C. Corbin

DOI: https://doi.org/10.1016/j.carbon.2024.119197

IF: 10.9

2024-05-01

Carbon

Abstract:The mass concentration of soot aggregates is often estimated from mobility size distributions using a mobility-based effective density, ρ eff . This ρ eff changes with aggregate morphology. In particular, the ρ eff of a soot core increases when it becomes compacted by the surface tension of condensing coatings, such as combustion-related vapours, secondary aerosols, and cloud water. The extent of this compaction is a function of coating volume, up to an asymptotic limit of complete compaction. While complete compaction has previously been shown to correspond to a universal, scale-invariant packing factor for sufficiently large aggregates, it has not previously been explicitly quantified. Here, we critically reanalyze multiple datasets compiled from the literature on the ρ eff of completely compact soot. We show that, regardless of the coating material, soot aggregates generally become completely compacted following a 5-fold increase in volume. The final aggregate shape is more simply described by ρ eff than by mobility diameter or shape factor. Below 140 nm diameter (about 20 aggregate monomers), the compacted ρ eff obeys a power law; above 140 nm, it reaches a constant value of 651 ± 8 kg m –3 . This ρ eff is 3 times larger than that of freshly-produced soot at 140 nm. We provide a parameterization of the compacted ρ eff for the estimation of soot mass concentration after coating, or, conversely, for use as a benchmark to estimate the extent of aggregate restructuring. Our parameterization can be easily adapted to other nanoparticle aggregates whose material density is known.

materials science, multidisciplinary,chemistry, physical