Surface modification of polysulfone/PAO40 microcapsules via polydopamine to improve thermal stability and used to prepare polyamide 6-based self-lubricating composite

Wenli Zhang,Xiaowen Qi,Xiaolei Li,Yu Dong,Weigang Yao,Lei Liang,Yan Zhang

DOI: https://doi.org/10.1016/j.colsurfa.2021.126906

2021-09-01

Abstract:<p>Herein, the modification of polydopamine (PDA) surface improved the high temperature stability of polysulfone (PSF)/PAO40 microcapsules (<span class="small-caps">D</span>-microcapsules), which achieved the potential application of microcapsules in polyamide 6 (PA6). The <span class="small-caps">D</span>-microcapsules in PA6 for lubricative application has been investigated by ball-on-disc friction tests. In particular, the inclusion of 9 wt% <span class="small-caps">D</span>-microcapsules yielded the best tribological properties where the value of COF (0.088) was largely decreased as compared with that of the neat PA6(0.41). Moreover, the wear rate was found to be decreased from 4 × 10⁻³ mm³/Nm to 4.3 × 10⁻⁶ mm³/Nm. It has been demonstrated that better antifriction performance was associated with the lubricating film generated by PAO40. Therefore, the prepared PA6-based self-lubricating composites can be further applied in the field of self-lubricating materials.</p>

chemistry, physical

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to improve the tribological properties of polyamide 6 (PA6), especially to reduce its friction coefficient and wear rate. As a typical engineering thermoplastic, PA6 is widely used in fields such as gears and bearings due to its low cost, high performance and good processability. However, as a friction material, the application of PA6 is limited by its high friction coefficient and high wear rate. To overcome this defect, researchers have tried various methods, such as filling with different solid fillers or additives to improve the tribological properties of PA6. However, solid lubricants have obvious deficiencies compared with liquid lubricants in reducing the friction coefficient, wear rate and self - repairing lubricating film.

Therefore, this paper proposes a liquid lubrication technology based on stress - stimulation - response. By preparing a new type of polydopamine (PDA) - surface - modified polysulfone (PSF)/poly - α - olefin 40 (PAO40) microcapsule (D - microcapsule) and adding it to the PA6 matrix, the tribological properties of PA6 are improved. Specifically, the research found that when the content of D - microcapsule is 9wt%, the friction coefficient of PA6 - based composite material is significantly reduced to 0.088, and the wear rate is also reduced from 4×10^(-3) mm³/Nm to 4.3×10^(-6) mm³/Nm, showing the best tribological properties. This is mainly because the D - microcapsules break during the friction process, releasing PAO40 oil and forming a stable lubricating film at the friction interface, thus effectively reducing friction and wear.

Through this method, this research not only improves the tribological properties of PA6 - based composite materials, but also provides new ideas for the application of self - lubricating microcapsules in engineering thermoplastics.