The preparation of a bisphenol A epoxy resin based ammonium polyphosphate ester and its effect on the char formation of fire resistant transparent coating

Xuelian Liu,Jia Guo,Jun Sun,Xiaoyu Gu,Weihua Feng,Wei Liu,Hongfei Li,Sheng Zhang

DOI: https://doi.org/10.1016/j.porgcoat.2019.01.003

IF: 6.6

2019-04-01

Progress in Organic Coatings

Abstract:This work reports the synthesis of an effective charring agent (ammonium polyphosphate ester (BAPPE)) and its application in preparing intumescent transparent fire resistive coatings. Bisphenol A epoxy resin reacted with diethanol amine to produce a waterborne epoxy resin (WEP), and then WEP was further reacted with orthophosphoric acid (PA) and urea (U) to obtain BAPPE. The chemical structure of BAPPE was confirmed by FT-IR and 1H NMR. Transparent fire resistive coating containing BAPPE and melamine urea formaldehyde (MUF) resin was prepared. The thermal gravimetric analysis showed that BAPPE could enhance char formation of the coating in the temperature range of 320–800 ℃. The flammability evaluation by simulated big panel method, smoke density test, and cone calorimeter (CONE) indicated that the presence of BAPPE significantly increased the fire resistant time, suppressed the smoke release amount, and remarkably reduced the peak heat release rate (pHRR) to 6.6 kW/m2. It was proved BAPPE could act as a three sources integrated reactive flame retardant in transparent coating. It is proposed that BAPPE can form cross-linking networks with MUF, thus enhancing the char formation upon heating and improving the fire resistance of the coating.

materials science, coatings & films,chemistry, applied