Microscopic Structural Evolution during Ultrastable Metallic Glass Formation
Peng Luo,Fan Zhu,Yu-Miao Lv,Zhen Lu,Lai-Quan Shen,Rui Zhao,Yi-Tao Sun,Gavin B. M. Vaughan,Marco di Michiel,Beatrice Ruta,Hai-Yang Bai,Wei-Hua Wang
DOI: https://doi.org/10.1021/acsami.1c10716
2021-08-10
Abstract:By decreasing the rate of physical vapor deposition, ZrCuAl metallic glasses with improved stability and mechanical performances can be formed, while the microscopic structural mechanisms remain unclear. Here, with scanning transmission electron microscopy and high-energy synchrotron X-ray diffraction, we found that the metallic glass deposited at a higher rate exhibits a heterogeneous structure with compositional fluctuations at a distance of a few nanometers, which gradually disappear on decreasing the deposition rate; eventually, a homogeneous structure is developed approaching ultrastability. This microscopic structural evolution suggests the existence of the following two dynamical processes during ultrastable metallic glass formation: a faster diffusion process driven by the kinetic energy of the depositing atoms, which results in nanoscale compositional fluctuations, and a slower collective relaxation process that eliminates the compositional and structural heterogeneity, equilibrates the deposited atoms, and strengthens the local atomic connectivity.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c10716.In-house XRD characterizations (Figure S1); AFM characterizations (Figure S2); typical sequential nanoindentation results (Figure S3); derivatives of the heat flow (Figure S4); estimation of the enthalpy change (Figure S5); and interatomic bond length, weight factor, and heat of mixing (Table S1) (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology