Abstract:The commonly used chitin whiskers (CHWs) prepared by the acid hydrolysis method are easy to agglomerate in an alkaline matrix, which limits their applications in many aspects. Herein, maleation chitin whiskers (mCHWs) with lots of −COOH groups were designed, which can stably exist and homogeneously disperse in the alkaline chitin matrix due to their relatively strong electronegativities. Subsequently, the CHWs and mCHWs were utilized as reinforcing fillers to enhance the mechanical strength of the chitin hydrogel. As expected, the CHWs played an extremely limited role in reinforcing the chitin hydrogel. Conversely, due to good dispersibility and strong interfacial interaction, the mCHWs exhibited a significantly superior enhancement effect on the chitin hydrogel. Moreover, the tensile strength and modulus of the as-prepared mCHW/chitin composite hydrogels were strongly dependent on the content of mCHWs, and the highest values of 5.8 ± 0.2 and 5.2 ± 0.6 MPa were obtained with 3 wt % mCHW content, which are higher than those of polysaccharide hydrogels reported in the most literature. Importantly, both CHWs and mCHWs can facilitate the adhesion, proliferation, and differentiation of mouse embryo osteoblast precursor (MC3T3-E1) cells. Moreover, the mCHWs also play these promoting effects in a content-dependent manner. Interestingly, CHWs and mCHWs mainly contain −NH<sub>2</sub> and −COOH groups, respectively; as a result, surface protein adsorption and calcium-phosphate mineralization are different. But there are very small differences in cell adhesion, proliferation, and differentiation between the corresponding 3%CHW/chitin and 3%mCHW/chitin composite hydrogels. This work provides a promising strategy to construct a polysaccharide nanocomposite hydrogel with robust mechanical strength and osteogenesis for potential application as an artificial periosteum.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c06411?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c06411</a>.The FTIR spectra of the purified chitin and chitin hydrogel (Figure S1); the tensile properties of chitin hydrogels prepared using different parameters (Figure S2); the length and diameter distribution of CHWs and mCHWs (Figure S3); the shrinkage degree of hydrogels after regeneration (Figure S4); and the tensile properties of CHW/chitin composite hydrogels with different contents of CHWs (Figure S5) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c06411/suppl_file/sc0c06411_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Photocurable liquid crystal hydrogels with different chargeability and tunable viscoelasticity based on chitin whiskers

Dual-Cross-linked Liquid Crystal Hydrogels with Controllable Viscoelasticity for Regulating Cell Behaviors

Chitin whisker/chitosan liquid crystal hydrogel assisted scaffolds with bone-like ECM microenvironment for bone regeneration

Engineering the Viscoelasticity of Gelatin Methacryloyl (gelma) Hydrogels Via Small “dynamic Bridges” to Regulate BMSC Behaviors for Osteochondral Regeneration

Mimicking the Mechanical Properties of Cartilage Using Ionic- and Hydrogen-Bond Cross-Linked Hydrogels with a High Equilibrium Water Content above 70%

Structural Design of Robust and Biocompatible Photonic Hydrogels from an in Situ Cross-Linked Hyperbranched Polymer System

Creating Ultrastrong and Osteogenic Chitin Nanocomposite Hydrogels via Chitin Whiskers with Different Surface Chemistries

Interpenetrating Polymer Network Hydrogels Composed of Chitosan and Photocrosslinkable Gelatin with Enhanced Mechanical Properties for Tissue Engineering

Multi-Crosslinked Strong and Elastic Bioglass/Chitosan-Cysteine Hydrogels with Controlled Quercetin Delivery for Bone Tissue Engineering

Abundant nucleation sites-available liquid crystal hydrogel mimics bone ECM mineralization to boost osteogenesis

Fabrication of physical and chemical crosslinked hydrogels for bone tissue engineering

An Injectable Hydrogel Formed by in Situ Cross-Linking of Glycol Chitosan and Multi-Benzaldehyde Functionalized Peg Analogues for Cartilage Tissue Engineering

Tunable and Fast-Cured Hyaluronic Acid Hydrogel Inspired on Catechol Architecture for Enhanced Adhesion Property

Biobased pH-responsive and self-healing hydrogels prepared from O-carboxymethyl chitosan and a 3-dimensional dynamer as cartilage engineering scaffold

Facile Construction of Hybrid Hydrogels with High Strength and Biocompatibility for Cranial Bone Regeneration

Synthesis and properties of high performance biobased liquid crystal copolyesters toward load-bearing bone repair application

Development of Gelatin Methacryloyl/Sodium Alginate Interpenetrating Polymer Network Hydrogels for Bone Regeneration by Activating the Wnt/β-Catenin Signaling Pathway via Lithium Release

Dynamic regulable sodium alginate/poly(γ-glutamic acid) hybrid hydrogels promoted chondrogenic differentiation of stem cells

Strong, elastic and degradation-tolerated hydrogels composed of chitosan, silk fibroin and bioglass nanoparticles with factor-bestowed activity for bone tissue engineering

Mechanically Robust Hydrogels Facilitating Bone Regeneration Through Epigenetic Modulation

Double crosslinking hydrogel with tunable properties for potential biomedical application