Abstract:The power conversion efficiency of perovskite solar cells (PSCs) has increased dramatically over the past decade, reaching more than 26%. With such high efficiency, PSCs could become one of the most important commercial alternatives to silicon‐based solar cells in the near future. However, the inconsistency of PSC operation over time is the key issue restricting its commercial application. One of the most common means of improving the overall stability of PSCs is the introduction of additives with specific functional groups to extend their useful life. Here we compare the performance and stability of MAPbI3‐based PSCs with additions of either benzoic acid (0F‐B), fluorinated benzoic acids (4‐fluorobenzoic acid (1F‐B), or 2,3,4,5,6‐pentafluorobenzoic acid (5F‐B)) in the perovskite active layer. These additives, upon interacting with the perovskite precursors, chelate onto lead ions and form hydrogen bond with methyl ammonium ions. These combined interactions result in an increased activation energy for nucleation of perovskite crystals, thereby, increased crystal size, reduced defect formation, improved electronic properties, as well as reduced ion migration. As a result, PSCs added with largest fluorine substitution of 5F‐B achieve the highest efficiency of 20.50% with a narrow PCE distribution compared to that of PSC devices added with 1F‐B (19.25%), 0F‐B (18.80%) and pristine devices (18.53%). Notably, 5F‐B added PSCs retain 80% of their initial PCE after ∽100 days humidity test (at 25 °C and 50 RH%), 30 days thermal stability test (at 85 °C in nitrogen environment), and 12 days light illumination test (continuous simulated solar radiation). Therefore, 5F‐B added PSCs synergistically achieve the highest performance and remain very stable under constant heat, humidity, or light illumination conditions for sustained energy‐harvesting applications in the future. TOC: This study focuses on the impacts of benzoic acid and its fluorinated derivatives functioning as effective passivation additives for methyl ammonium lead iodide (MAPbI3) perovskite solar cells. These additives synergistically passivate the perovskite layer, resulting in improved crystallinity and surface morphology, leading to an increased efficiency. Moreover, this approach enhances the long‐term stability of the architected solar cells, rendering them more suitable for future commercial applications. This article is protected by copyright. All rights reserved.

Constructing Additives Synergy Strategy to Doctor‐Blade Efficient CH3NH3PbI3 Perovskite Solar Cells under a Wide Range of Humidity from 45% to 82%

Constructing Additives Synergy Strategy to Doctor-Blade Efficient CH3 NH3 PbI3 Perovskite Solar Cells under a Wide Range of Humidity from 45% to 82.

Phase Engineering of Perovskite Materials for High-Efficiency Solar Cells: Rapid Conversion of CH3NH3PbI3 to Phase-Pure CH3NH3PbCl3 Via Hydrochloric Acid Vapor Annealing Post-Treatment

Benefitting from Synergistic Effect of Anion and Cation in Antimony Acetate for Stable CH3NH3PbI3-Based Perovskite Solar Cell with Efficiency Beyond 21%

Benefitting from Synergistic Effect of Anion and Cation in Antimony Acetate for Stable CH3 NH3 PbI3 -Based Perovskite Solar Cell with Efficiency Beyond 21

Additive-Regulated One-Step Dynamic Spin-Coating for Fabricating High-Performance Perovskite Solar Cells under High Humidity Conditions

Crystallization and Defect Chemistry Dual Engineering for MAPbI 3 Perovskite Solar Cells with Efficiency Approaching 22%

Synergetic Excess PbI2 and Reduced Pb Leakage Management Strategy for 24.28% Efficient, Stable and Eco‐Friendly Perovskite Solar Cells

Ultrahigh Fill-Factor All-Inorganic CsPbBr3 Perovskite Solar Cells Processed from Two-Step Solution Method and Solvent Additive Strategy

CH 3 NH 3 PbBr 3– x I x Quantum Dots Enhance Bulk Crystallization and Interface Charge Transfer for Efficient and Stable Perovskite Solar Cells

A Multifunctional Additive Strategy to Stabilize the Precursor Solution and Passivate Film Defects for MA-free Perovskite Solar Cells with an Efficiency of 22.75%

Multistrategy Toward Highly Efficient and Stable CsPbI 2 Br Perovskite Solar Cells Based on Dopant‐Free Poly(3‐Hexylthiophene)

Synergistic Enhancement of Stability and Performance for Perovskite Solar Cells Using Fluorinated Benzoic Acids as Additives

An Extraordinary Antisolvent Ethyl Cyanoformate for Achieving High Efficiency and Stability P3HT‐Based CsPbI3 Perovskite Solar Cells

Enhancing Performance and Stability of Perovskite Solar Cells with a Novel Formamidine Group Additive

Improving Moisture/Thermal Stability and Efficiency of CH3NH3PbI3‐Based Perovskite Solar Cells Via Gentle Butyl Acrylate Additive Strategy

Controllable Cosolvent Blade-Coating Strategy Toward Low-Temperature Fabrication of Perovskite Solar Cells

Enhanced efficiency of planar perovskite solar cells via a two-step deposition using DMF as an additive to optimize the crystal growth behavior

Synergistic Effect of Defects Passivation and Energy Level Alignment Realizing P3HT‐Based High‐Efficiency CsPbI3 Perovskite Solar Cells

Multistrategy Toward Highly Efficient and Stable CsPbI2Br Perovskite Solar Cells Based on Dopant‐Free Poly(3‐Hexylthiophene)

Synergistic effect of MACl and DMF towards efficient perovskite solar cells