Highly efficient GO-based synergistic intumescent flame retardant/thermoplastic polyurethane for spatial composite film: insight into flame retardancy and mechanism
Weijie Zheng,Qingshu Cai,Lei Xiong,Yuying Zheng
DOI: https://doi.org/10.1007/s10973-024-13273-7
IF: 4.755
2024-06-20
Journal of Thermal Analysis and Calorimetry
Abstract:In recent years, thermoplastic polyurethane elastomer has shown great application prospects in the fields of polymer film due to its outstanding tensile properties, high elasticity, wear resistance, oil resistance, low temperature resistance, wide range of hardness, and other properties. However, its flammable properties greatly limit its application in the field of polymer film. The self-made GO was used as a carbon source, phenylboronic acid as an acid source, ammonium polyphosphate (APP) as an acid and gas source, and intumescent flame retardant (IFR) was compounded. The IFR was introduced into thermoplastic polyurethane (TPU) to prepare a series of IFR/TPU composite films with different formulations. The results show that PA and GO can make up for the loss of mechanical properties caused by the addition of APP and improve the thermal stability of the composite film, and the IFR flame retardant composed of the two and APP can effectively improve the flame retardancy of the composite film. When the additions of APP, PA, and GO were 10, 3, and 0.75%, respectively, the LOI value of the IFR/TPU composite material reached 29.5, the flame-retardant grade reached V-0, and its peak heat release rate, total heat release, peak smoke production rate, and total smoke release were 86.0, 64.9, 70.5, and 21.7%, greatly lower than pure TPU, respectively. The flame retardancy of the spacer composite membrane constructed from Ti-7 was significantly improved, and the burn-through time of the single-layer film sample was increased by 2.22 times, and the double-layer film sample was increased by 2.63 times.
chemistry, physical, analytical,thermodynamics