Ylenia Ruberto,Vera Vivod,Janja Juhant Grkman,Gregor Lavrič,Claudia Graiff,Vanja Kokol
Abstract:Cellulose nanocrystals (CNCs) and chitosan (Cht) have been studied extensively for oxygen and water vapour barrier coatings in biodegradable, compostable or recyclable paper packaging. However, rare studies have been performed by using scalable, inexpensive, and fast continuous slot-die coating processes, and none yet in combination with fast' and high-throughput near-infrared (NIR) light energy drying. In this frame, we studied the feasibility of a moderately concentrated (11 wt%) anionic CNC and (2 wt%) cationic Cht coating (both containing 20 wt% sorbitol related to the weight of CNC/Cht), by using plain and pigment pre-treated papers. The effect of coating parameters (injection speed, dry thickness settings) were investigated on coating quantity (dry weight, thickness) and homogeneity (coverage), papers' structure (thickness, grammage, density), whiteness, surface wettability, barrier (air, oxygen and water vapour) properties and adhesion (surface strength). The coating homogeneity was dependent primarily on the suspensions' viscosity, and secondarily on the applied coating parameters, whereby CNCs could be applied at 1–2 times higher injection speeds (up to 80 mL/min) and versatile coating weights, but required a relatively longer time to dry. The CNCs thus exhibited outstanding air (4.2–1.5 nm/Pa s) and oxygen (2.7–1.1 cm 3 mm/m 2 d kPa) barrier performance at 50% RH and 22–33 g/m 2 deposition, whereas on top deposited Cht (3–4 g/m 2 ) reduced its wetting time and improved the water vapour barrier (0.23–0.28 g mm/m 2 d Pa). The balanced barrier properties were achieved due to the polar characteristic of CNCs, the hydrophobic nature of Cht and the quantity of the applied bilayer coating that can provide sustainable paper-based packaging.
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the barrier properties of paper by using slot - die coating technology in combination with near - infrared (NIR) drying technology. Specifically, the researchers hope to improve the barrier properties of paper against air, oxygen and water vapor by coating a mixture of cellulose nanocrystals (CNCs) and chitosan (Cht) on ordinary paper and pretreated paper (containing calcium carbonate particles, starch as a binder and carboxymethyl cellulose as a co - binder). In addition, the study also explored the effects of different coating parameters (such as injection speed, dry coating thickness setting) on the coating amount, uniformity, as well as paper structure characteristics (such as thickness, grammage, density), whiteness, surface wettability, barrier properties (air, oxygen and water vapor permeability) and adhesion (surface strength).
### Research Background
Due to its porosity and hydrophilicity, paper has a natural deficiency in barrier properties in various packaging applications (such as pharmaceuticals, food, medical). Therefore, the use of biopolymer - based surface coatings is a common improvement method, especially in order to follow the principles of circular economy and overall sustainability. Cellulose nanocrystals (CNCs) and chitosan (Cht) have been widely studied for improving the air and oxygen barrier properties of paper because of their high oxygen - molecule interaction ability and as matrices for other additives (such as antibacterial agents, antioxidants, nutrients, etc.). However, the low water - vapor barrier property of these biopolymers is a major drawback, which can be partially improved by using water - insoluble biopolymers such as chitosan.
### Research Methods
The study adopted slot - die coating technology, using 11 wt% CNC suspension and 2 wt% Cht solution, as well as their mixture (5.5 wt% CNC and 1 wt% Cht), for coating in laboratory automation equipment, combined with high - performance near - infrared drying technology. The study evaluated the effects of coating parameters (injection speed, dry coating thickness setting) on coating retention performance, coating amount and uniformity, paper physical characteristics (grammage, thickness, density) and whiteness. At the same time, the influence of the coating on the paper structure was also analyzed, especially the air, oxygen and water vapor permeability and surface wettability (surface hydrophobicity).
### Main Findings
1. **Coating Uniformity and Thickness**: The CNC suspension can be evenly spread at a higher injection speed (up to 80 mL/min), while the Cht solution is limited to a lower injection speed (about 30 mL/min). This may be due to the different surface tensions and visco - capillary forces of the two liquids.
2. **Barrier Properties**: The CNC + Cht mixture can significantly increase the thickness of the paper (27.6% - 39.3%) and greatly reduce the air flow rate (about 76.7%) at a lower coating weight (6.3 - 12.7 g/m²). For pretreated paper, the reduction in air flow rate is more significant, and can even reach 97.8% reduction at a lower coating weight (6.33 g/m²).
3. **Double - layer Coating Effect**: A 22 g/m² 11 wt% CNCs coating, plus a 3 g/m² 2 wt% Cht coating, makes the paper almost air - tight, and the air flow rates are reduced to 0.01 mL/min (for ordinary paper) and 0.5 mL/min (for pretreated paper) respectively.
4. **NIR Drying Effect**: NIR drying technology can quickly and effectively remove the moisture in the coating without affecting the integrity and uniformity of the coating.
### Conclusion
By optimizing the slot - die coating technology and NIR drying technology, the barrier properties of paper can be significantly improved, especially in terms of air, oxygen and water - vapor barriers. The combined coating of CNC and Cht not only improves the barrier properties of paper, but also improves its surface uniformity and mechanical properties, providing a new way for the development of sustainable packaging materials.