Efficient Blade‐Coated Wide‐Bandgap and Tandem Perovskite Solar Cells via a Three‐Step Restraining Strategy
Hongyi Fang,Weicheng Shen,Hongling Guan,Guoyi Chen,Guang Li,Wei Ai,Shiqiang Fu,Zuxiong Xu,Weiqing Chen,Peng Jia,Zixi Yu,Shuxin Wang,Zhiqiu Yu,Qingxian Lin,Jiahao Wang,Wenwen Zheng,Dexin Pu,Guojia Fang,Weijun Ke
DOI: https://doi.org/10.1002/adma.202414790
IF: 29.4
2024-11-24
Advanced Materials
Abstract:Strict control of crystal growth has historically limited the efficiency of blade‐coated perovskite solar cells compared to spin‐coated devices. Here, a three‐step restraining strategy that employs a functional additive to regulate crystal growth enables efficient blade‐coated perovskite solar cells. This approach achieves a 19.97% efficiency for single‐junction 1.77 eV wide‐bandgap cells and a 27.11% efficiency for 2‐terminal all‐perovskite tandem solar cells. Blade‐coating techniques have attracted significant attention for perovskite solar cells (PSCs) due to their high precursor utilization and simplicity. However, the power conversion efficiency (PCE) of blade‐coated PSCs often lags behind that of spin‐coated devices, mainly due to difficulties in precisely controlling perovskite film formation during pre‐nucleation, heterogeneous nucleation, and crystallization in the blade‐coating and N2‐knife drying processes. In this work, a three‐step restraining strategy is introduced utilizing functional glycine amide hydrochloride to regulate pre‐nucleation clustering, suppress excessive heterogeneous nucleation, and decelerate crystallization, enabling comprehensive control of the perovskite film formation processes. This approach results in enlarged grains, reduced defect densities, and highly oriented crystalline wide‐bandgap perovskite films with significantly prolonged carrier lifetimes, achieving a maximum PCE of 19.97% for 1.77 eV‐bandgap blade‐coated PSCs. Furthermore, two‐terminal tandem cells, composed of wide‐bandgap perovskite top cells and 1.25 eV‐bandgap perovskite bottom cells fabricated via blade coating, yield an impressive PCE of 27.11% (stabilized at 26.87%). This study offers comprehensive insights into controlling pre‐nucleation, heterogeneous nucleation, and crystallization during blade coating, providing valuable guidance for developing high‐performance, large‐area devices in the future.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology