Fabrication of rGO/CdS@2H, 1T, amorphous MoS2 heterostructure for enhanced photocatalytic and electrocatalytic activity

Yue Zhao,Xiao Zhang,Tao Wang,Tong Song,Ping Yang
DOI: https://doi.org/10.1016/j.ijhydene.2020.05.217
IF: 7.2
2020-08-01
International Journal of Hydrogen Energy
Abstract:<p>The synthesis of high efficiency noble metal free catalysts is an important target for H<sub>2</sub> production by water-splitting. In this work, rGO/<sub>2</sub> heterostructure with two catalytic paths was successfully synthesized and as the first applied the heterostructure in the field of electrocatalysis. The MoS<sub>2</sub> structure is adjusted by controlling hydrothermal process. Moreover, the effects of structure and loading amount of 2H–MoS<sub>2</sub>, 1T-MoS<sub>2</sub> and amorphous MoS<sub>2</sub> (A-MoS<sub>2</sub>) on catalytic performance were also studied. The catalytic activity of rGO/<sub>2</sub> heterostructure has been improved obviously. Compared with 2H–MoS<sub>2</sub>, the distortion of 1T-MoS<sub>2</sub> and the defect of A-MoS<sub>2</sub> make it have more unsaturated S, so rGO/<sub>2</sub> and rGO/<sub>2</sub> have better catalytic activity. For photocatalytic H<sub>2</sub> evolution, loading MoS<sub>2</sub> and rGO on catalysts changes the energy band structure, promotes the separation of electron-holes and provides a large number of active sites. Among them, the visible light photocatalytic H<sub>2</sub> production rate of rGO/<sub>2</sub> with 0.1 mol of 1T-MoS<sub>2</sub> (CT0.1-G1) is 18.26 mmol/g/h. During the electrocatalytic H<sub>2</sub> evolution, introducing MoS<sub>2</sub> and rGO improves electronic structure and increases active sites. rGO/<sub>2</sub> with 0.5 mol of 1T-MoS<sub>2</sub> (CT0.5-G1) shows the low overpotential (312 mV) and Tafel slopes (85 mV/dec).</p>
energy & fuels,electrochemistry,chemistry, physical
What problem does this paper attempt to address?