Fabrication and characterizations of Cr 3+ ‐doped ZnGa 2 O 4 transparent ceramics with persistent luminescence

Qiang Liu,Xinyu Mao,Xiaoying Li,Penghui Chen,Xin Liu,Ziyu Liu,Danyang Zhu,Haohong Chen,Tengfei Xie,Jiang Li

DOI: https://doi.org/10.1111/jace.17937

IF: 4.186

2021-06-08

Journal of the American Ceramic Society

Abstract:<p>0.5 at.% Cr:ZnGa₂O₄ precursor was synthesized by the co-precipitation method with nitrates as raw materials, using ammonium carbonate as the precipitant. Low-agglomerated Cr:ZnGa₂O₄ powders with the average particle size of 43 nm was obtained by calcining the precursor at 900 °C for 4 h. Using the powders as starting materials, 0.5 at.% Cr:ZnGa₂O₄ ceramics with the average grain size of about 515 nm were prepared by pre-sintering at 1150 °C for 5 h in air and HIP post-treatment at 1100 °C for 3 h under 200 MPa Ar. The in-line transmittance of 0.5 at.% Cr:ZnGa₂O₄ ceramics with the thickness of 1.3 mm reaches 59.5% at the wavelength of 700 nm. The Cr:ZnGa₂O₄ ceramics can be effectively excited by visible light and produce persistent luminescence at 700 nm. For Cr:ZnGa₂O₄ transparent ceramics, the brightness of afterglow was larger than 0.32 mcd/m² after 30 min, which is far superior to that of Cr:ZnGa₂O₄ persistent luminescence powders.</p>

materials science, ceramics