Abstract:This paper discusses two different mechanisms of temperature effects on magnetoimpedance (MI), namely, the internal stress relaxation upon heating and critical behavior of magnetic parameters near the Curie temperature T c . When a microwire is heated, the residual stress is partially released changing the effective anisotropy, which inevitably leads to the temperature dependence of hysteresis and MI. A very large change in impedance up to 200% with moderate temperature increase (50–70 °C) occurs in microwires of Co66.94Fe3.83Ni1.44 B11.51Si14.59Mo1.69 compositions with high T c ≈ 340 ° C where the magnetostriction changes a sign from negative to positive due to stress relaxation. Proper annealing is demonstrated to stabilize such temperature variations in MI. Near the Curie temperature, the impedance undergoes large variations due to a corresponding drop in the magnetization saturation and magnetic anisotropy. The theoretical modelling reveals an increase in the dc initial permeability when approaching T c , which results in different temperature behaviours of MI at low and high frequencies. This was confirmed experimentally for Co23.67Fe7.14Ni43.08B13.85Si12.26 amorphous microwires ( T c  = 62 °C): at a frequency of 10 MHz the impedance increases with temperature until very close proximity of T c , whilst at a frequency of 300 MHz it continuously decreases with increasing temperature. Controlling the value of T c the impedance temperature dependence can be realized in the industrial temperature range of 20–100 °C. This has potential applications for developing embedded miniature temperature sensors.

The Influence of Relaxation Annealing on the Magnetic Properties and Magnetic Impedance of Amorphous Co-Based Wires

Effect of Annealing Temperature on Permeability and Giant Magneto-Impedance of Fe-based Amorphous Ribbon

Temperature Dependence of the Off‐diagonal Magnetoimpedance in Sensor Configuration Utilizing Co‐rich Amorphous Wires

Evolution of the Magnetic Anisotropy and Magnetostriction in Co-based Amorphous Alloys Microwires Due to Current Annealing and Stress -Sensory Applications

Temperature-stable magnetoimpedance (MI) of current-annealed Co-based amorphous microwires

Effect of Tension Annealing on Giant Magneto-Impedance in Glass-Covered Co-rich Amorphous Wire

Temperature Dependence of Magnetic Property for Glass-Coated Metal Microwires

Effect of Annealing on the Magnetostatic and Microwave Electromagnetic Properties of Glass-Coated Fe-Rich Microwires

Enhancing GMI properties of melt-extracted Co-based amorphous wires by twin-zone Joule annealing

Special Stress-Magnetization Properties in Co-Based Amorphous Wire

Temperature Dependences of the High-Frequency Electrical Impedance of Cobalt-Based Amorphous Wires with an Inhomogeneous Magnetic Structure

Temperature effects in Co-based amorphous wires

Comparative Study on Magnetic Properties and Microstructure of As-prepared and Alternating Current Joule Annealed Wires

Magnetic anisotropy and stress-magnetoimpedance (S-MI) in current-annealed Co-rich glass-coated microwires with positive magnetostriction

Correlation of Magnetic Domains, Microstructure and Gmi Effect of Joule-Annealed Melt-Extracted Co68.15fe4.35si12.25b13.75nb1cu0.5 Microwires for Double Functional Sensors

Combined Current-Modulation Annealing Induced Enhancement Of Giant Magnetoimpedance Effect Of Co-Rich Amorphous Microwires

Annealing Temperature Dependance of Magnetic Properties and Magneto-Impedance Effect in CoZrB Alloys

Temperature effects on magnetization processes and magnetoimpedance in low magnetostrictive amorphous microwires

Magnetic properties of the amorphous Co-Fe-Cr-Si-B alloy after annealing in unsaturated magnetic field

Improving Mechanical and Magnetocaloric Responses of Amorphous Melt-Extracted Gd-based Microwires Via Nanocrystallization

Effect of annealing in unsaturated magnetic field on the magnetic properties of an amorphous alloy Fe77Ni1Si9B13