Ultrahigh Pt-mass-activity Catalyst for Alkaline Hydrogen Evolution Synthesized by Microwave Method in Air
Yirui Jiang,Jianfang Liu,Hongru Liu,Yong Wang,Yongzhi Zhao,Sijia Liu,Yunpu Qin,Zihao Li,Hong Zhao,Hao Li,Haoyang Wu,Deyin Zhang,Luan Liu,Baorui Jia,Xuanhui Qu,Mingli Qin
DOI: https://doi.org/10.1016/j.ceramint.2024.06.286
IF: 5.532
2024-01-01
Ceramics International
Abstract:Platinum (Pt) metal is widely acknowledged as a highly efficient electrocatalyst for hydrogen evolution reaction (HER) in acidic electrolyte. However, its performance in alkaline environments is significantly lower owing to the sluggish water dissociation step. Herein, we synthesized an ultrahigh Pt-mass-activity alkaline HER catalyst using microwave reduction method in air. Our catalyst, PtRu@CNT, comprises PtRu alloy nanoparticles uniformly loaded on carbon nanotubes, with Pt and Ru contents of 12.3 wt% and 4.5 wt%, respectively. The PtRu alloy nanoparticles have an average diameter of about 3 nm and a face-centered cubic structure, and the introduction of Ru has led to a modified electronic structure in Pt. As a result, an impressively low HER overpotential of 13 mV was achieved, significantly lower than commercial 20 wt% Pt/C (61 mV). PtRu@CNT exhibited a high turnover frequency based on metal mass of 3.06 s- 1 at 100 mV, about 6 times higher than commercial Pt/C (0.46 s- 1 at 100 mV), highlighting its excellent intrinsic activity. The HER mechanism of PtRu@CNT is a Volmer-Tafel mechanism, where the rate-limiting step changed to the recombination of hydrogen atoms from initial water dissociation, attributed to the presence of Ru. The alkaline HER activity of PtRu@CNT ranks among the best of currently reported Pt-based catalysts.