Abstract:Cu/SiO2 catalyst prepared by the ammonia-evaporation (AE) method is the potential preferred catalyst for hydrogenation of dimethyl oxalate (DMO) to ethylene glycol (EG). Although significant advancements have been obtained in the confirmation and influence factors of active species in the hydrogenation process, the relationship between the catalytic activity and the sensitive factors in the preparation or pretreatment process of the catalyst is still uncertain. In this paper, Cu/ZSM-5 catalysts for DMO hydrogenation to EG were prepared by the AE method using ZSM-5 molecular sieve with high silicon-alumina ratio (1500) as a support. The ZSM-5 support was pretreated by drying at 393 K for different hours and it was found that the surface hydroxyl group of the support had significant influence on the structure and catalytic hydrogenation performance of the prepared Cu/ZSM-5 catalyst. The distribution of surface hydroxyl groups could be significantly changed by pre-drying the carrier, which further resulted in the change of the copper dispersion and surface properties of subsequent copper-supported catalysts. With the decrease of hydroxyl content on the surface of the ZSM-5 support, the prepared reduced Cu/ZSM-5 catalyst possessed smaller Cu0 particles size, higher copper dispersion, higher surface area of Cu0 and Cu+ species, but weakened surface acidity of the catalyst, which resulted in the great improvement of the catalytic activity. The DMO conversion and EG selectivity could reach 100% and 93% even under the low reaction temperature at 448 K over the Cu/ZSM-5-24 catalyst (based on the ZSM-5 support pretreated by drying for 24 h). In addition, the catalytic activity did not show obvious change after 300 h of reaction, probably due to the low temperature reaction and suitable surface properties of the catalyst.Graphical Abstract

Synthesis of a high surface area and highly dispersed Cu-O-Si complex oxide used for the low-temperature hydrogenation of dimethyl oxalate to ethylene glycol

Ultra-stable Cu-based catalyst for dimethyl oxalate hydrogenation to ethylene glycol

Preparation and modification of Cu/SiO2 catalyst for hydrogenation of dimethyl oxalate to ethyl glycol

Enhanced catalytic stability of Cu-based catalyst for dimethyl oxalate hydrogenation

Performance Enhancement of Cu/SiO2 Catalyst for Hydrogenation of Dimethyl Oxalate to Ethylene Glycol Through Zinc Incorporation

Facile preparation of efficient Cu-SiO 2 catalysts using a polyhydroxy molecular template to regulate surface copper species for dimethyl oxalate hydrogenation

Cu/SiO 2 hybrid catalysts containing HZSM-5 with enhanced activity and stability for selective hydrogenation of dimethyl oxalate to ethylene glycol

Efficient Tuning of Surface Copper Species of Cu/SiO2 Catalyst for Hydrogenation of Dimethyl Oxalate to Ethylene Glycol

Preparation of Cu-MCM-41 Catalyst and Catalytic Performance for Hydrogenation of Dimethyl Oxalate to Ethylene Glycol

Cu/Sio2 Catalysts Prepared by the Sol-Gel Method for Hydrogenation of Dimethyl Oxalate to Ethylene Glycol

Hydrogenation of Dimethyl Oxalate Using Extruded Cu/SiO2 Catalysts: Mechanical Strength and Catalytic Performance

Lanthanum oxide-modified Cu/SiO2 as a high-performance catalyst for chemoselective hydrogenation of dimethyl oxalate to ethylene glycol

Cu Active Sites Confined in MgAl Layered Double Hydroxide for Hydrogenation of Dimethyl Oxalate to Ethanol

Hydrogenation of Dimethyl Oxalate to Ethylene Glycol on A Cu/Sio2/Cordierite Monolithic Catalyst: Enhanced Internal Mass Transfer and Stability

Enhanced Catalytic Performance for SiO2–TiO2 Binary Oxide Supported Cu-based Catalyst in the Hydrogenation of Dimethyloxalate

Highly dispersed, ultra-small and noble metal-free Cu nanodots supported on porous SiO2 and their excellent catalytic hydrogenation of dimethyl oxalate to methyl glycolate

Role of the Cu dopant in the textural and catalytic features of the Co/ZnO catalyst for dimethyl oxalate selective hydrogenation

Superior silicon-free Cu catalyst for dimethyl oxalate hydrogenation: Exploring interaction between Cu and pyridinic-N-rich ultrathin carbon

Insights into a New Formation Mechanism of Robust Cu/SiO2 Catalysts for Low-Temperature Dimethyl Oxalate Hydrogenation Induced by a Chelating Ligand of EDTA

Effect of Surface Hydroxyl Content of Support on the Activity of Cu/ZSM-5 Catalyst for Low-Temperature Hydrogenation of Dimethyl Oxalate to Ethylene Glycol

Highly Active and Selective Cu/Sio2 Catalysts Prepared by the Urea Hydrolysis Method in Dimethyl Oxalate Hydrogenation