Abstract:This study investigates the impact of the chemical composition of superabsorbent polymers (SAPs) on their effectiveness in internal curing within high-performance cementitious materials. Although the use of commercial SAPs in cementitious systems has been widely researched, there is still no consensus on how different SAP structures influence material properties. For the first time, this research employs photoinitiated free radical polymerization technology to synthesize three structurally distinct SAPs: SAP with sulfonic acid groups (PAMPS), SAP with amide groups (PAM), and SAP with carboxyl groups (PAAs). The effects of these SAPs on the cement hydration process and microstructure were examined by analyzing their water absorption behavior in cement filtrate. The residual cation content on the SAP surface was evaluated using EDS, while XRD and TGA were used to study how SAP structure affects cement hydration products. Furthermore, the impact of these SAPs on the strength and autogenous shrinkage of the material was investigated. The results indicate that PAMPS, with its sulfonic acid groups, exhibited stable water absorption performance in the alkaline cement environment, promoting hydration reactions and increasing the formation of needle-shaped C-S-H. This stability contributed to mitigating the negative effects on mechanical properties. While the inclusion of SAPs generally reduced the strength of the cement matrix, PAMPS was the most effective in mitigating autogenous shrinkage, achieving a shrinkage mitigation efficiency of 86 %. These findings highlight the importance of SAP chemical structure in influencing cement hydration and material performance, offering insights for the development of effective internal curing agents to enhance high-performance concrete.

Internal curing by superabsorbent polymers in alkali-activated slag

Properties and Microstructure of Alkali-Activated Slag Paste Modified by Superabsorbent Polymers

Understanding the Shrinkage Behaviour of Alkali-Activated Slag Binders Modified by the Superabsorbent Polymer

The Influence of Nano-Silica Composite Superabsorbent Polymer on the Autogenous Shrinkage of Mortar

Effect of superabsorbent polymer introduction on properties of alkali-activated slag mortar

Improving internal curing efficiency through adjusting ab- and desorption curve of superabsorbent polymer in cement pastes using sodium carbonate

Internal curing with superabsorbent polymer modified by nano SiO 2 : Shrinkage mitigation and microstructure refinement

The Effect of Superabsorbent Polymers on Mechanical Characteristics and Cracking Susceptibility of Alkali-Activated Mortars Containing Ground Granulated Blast-Furnace Slag and Copper Slag

Exploring the Role of SAP Chemical Composition in the Internal Curing of High-Performance Cementitious Materials

Autogenous shrinkage of alkali-activated slag: A critical review

Influence of liquid-binder ratio on the performance of alkali-activated slag mortar with superabsorbent polymer

Internal curing of natural hydraulic lime with superabsorbent polymers

Mitigating Autogenous Shrinkage of Alkali-Activated Slag Mortar by Using Porous Fine Aggregates as Internal Curing Agents

Effects of alkali dosage and silicate modulus on autogenous shrinkage of alkali-activated slag cement paste

Shrinkage and Cracking of Cement Composites Containing Internal Curing Stuff

Mechanisms of autogenous shrinkage of alkali-activated slag and fly ash pastes

The Effect of Different Types of Internal Curing Liquid on the Properties of Alkali-Activated Slag (AAS) Mortar

Internal Curing Effect of Pre-Soaked Zeolite Sand on the Performance of Alkali-Activated Slag

Autogenous and Drying Shrinkage of Alkali‐activated Slag Mortars

Internal Relative Humidity, Autogenous Shrinkage, and Strength of Cement Mortar Modified with Superabsorbent Polymers

Robust evaluation of superabsorbent polymers as an internal curing agent in cementitious composites