Efficient Ozone Decomposition by Optimizing Defect Sites of NiMn-layered Double Hydroxides under High Humidity Air

Hongyang Jin,Zhen Li,Xin Min,Lei Zhong,Ke Chen,Songjian Zhao
DOI: https://doi.org/10.1016/j.jece.2024.114858
IF: 7.7
2024-01-01
Journal of Environmental Chemical Engineering
Abstract:Ozone is a pollutant that is very harmful to the ecological environment and human health, and layered double hydroxides (LDHs) have attracted much attention in recent years as an excellent anti-aqueous ozone catalyst. A kind of NiMn-LDHs with high defective sites was prepared by a one-step hydrothermal method to catalyze the degradation of ozone. The catalytic activity of NiMn-LDHs against ozone was further enhanced by increasing the concentration of oxygen vacancies on the surface while ensuring the intact structure of LDHs. When Ni/Mn=6:1, the catalyst had the best catalytic performance as well as stability, with 99.3% degradation efficiency for 50 ppm ozone after 24h of operation at WHSV=400000mL·g-1·h-1 and RH=60%. A series of data show that Ni6Mn-LDHs forms a crystal structure with lower crystallinity, larger specific surface area and smaller grain size. Compared with Ni2Mn-LDHs, the specific surface area of Ni6Mn-LDHs increased from 32.2 m2·g-1 to 171.4 m2·g-1, which is favourable to expose more surface defects. XPS and EPR confirmed that Ni6Mn-LDHs exhibited more surface oxygen vacancies, which plays a key role in the ozone decomposition process. The present study provides important guidance for the developed gaseous ozonolysis catalysts and promotes the practical ozone degradation performance of LDHs.
What problem does this paper attempt to address?