Li/Na Ion Storage Performance of a FeOF Nano Rod with Controllable Morphology
Linhua Li,Liangshun Xiang,Yan Lin,Lei Chen,Renqing Guo,Yiqi Cao,Xiaohua Huang,Jianbo Wu
DOI: https://doi.org/10.3390/pr10081491
IF: 3.5
2022-01-01
Processes
Abstract:Although the conversion material iron oxyfluoride (FeOF) possesses a high theoretical specific capacity as a cathode material for Li/Na ion batteries, its poor rate and cycling performances, caused mainly by sluggish (Li+/Na+) reaction kinetics, restrict its practical application. Herein, FeOF with high purity, a fusiform nanorod shape and high crystallinity is prepared through a facile chemical solution reaction. The electrochemical measurements show that the present FeOF exhibits high capacity and good cycling stability as a cathode material for Li-ion batteries. Capacities of 301, 274, 249, 222, and 194 mAh/g at stepwise current densities of 20, 50, 100, 200, and 400 mA/g are achieved, respectively. Additionally, the capacity at 100 mA/g retains 123 mAh/g after 140 cycles. Meanwhile, as a cathode material for Na ion battery, it delivers discharge capacities of 185, 167, 151, 134 and 115 mAh/g at stepwise current densities of 20, 50, 100, 200, and 400 mA/g, respectively. A discharge capacity of 83 mAh/g at 100 mA/g is achieved after 140 cycles. The excellent lithium/sodium-storage performance of the present FeOF material is ascribed to its unique nanostructure.