In Situ Well-Aligned Microfibrils and Mother-Daughter Crystals As Promising Blocks to Suppress Carrier Transport in Polypropylene Dielectric Films

De-Long Li,Chun-Yan Liu,Yue Li,Ling Xu,Jun Lei,Gan-Ji Zhong,Hua-Dong Huang,Zhong-Ming Li

DOI: https://doi.org/10.1021/acs.macromol.4c01640

IF: 5.5

2024-01-01

Macromolecules

Abstract:High-performance dielectric capacitors are essential for advanced electronics and electrical power systems. Nonetheless, the enhanced discharged energy density (U d) of polymer-based dielectric films is frequently accompanied by increased conduction and polarization losses as well as reduced charge-discharge efficiency (eta). In this study, a scalable "melting extrusion-hot stretching-solid-state stretching" technique was proposed to fabricate high-performance polypropylene (PP)/poly(ethylene terephthalate) (PET) all-organic dielectric films. During hot stretching, PET microdroplets deformed into microfibrils in situ, establishing massive parallel interfaces. The subsequent solid-state stretching induced a mesophase-to-alpha-crystal transition, forming a mother-daughter crystalline structure. The synergistic effect of well-aligned microfibrillar interfaces and the dense mother-daughter crystalline structure could significantly enhance the breakdown strength and capacitive storage capability by suppressing carrier transport. As a result, the as-prepared PP/PET dielectric films demonstrated an exceptional breakdown strength of 672.2 MV m-1 and a maximum U d of 4.11 J cm-3 with an eta of as high as 92.8%. The proposed technique is demonstrated to be highly effective for structuring in situ well-aligned microfibrils and mother-daughter crystalline structures, thus promoting the development of next-generation, high-performance PP-based film capacitors.