Abstract:Application of carbon-negative biochar in cement composites can effectively reduce carbon emissions of construction materials. However, strength reduction would be inevitable for the cement composites after the incorporation of high-volume porous biochar. Carbonated enhancement of interfacial transition zone (ITZ) in biochar-cement composite was developed by utilizing engineered biochar and CO2 curing to compensate for the strength degradation. The impact of biochar customized with different temperatures and activation methods on facilitating cement carbonation was explored. The increase of pyrolysis temperature and/or the application of CO2 or steam activation for biochar preparation could increase water absorption rate and CO2 adsorption capacity during subsequent CO2 curing, thus promoting the degree of cement hydration and carbonation. Carbonated ITZ mainly composed of CaCO3 with an elastic module range of 15-25 GPa would generate and surround the customized biochar (e.g., biochar prepared at 750 degrees C with CO2 activation). The results show that the samples with 10 wt% biochar incorporation under CO2 curing could achieve lower density and comparable compressive strength with the pure cement systems that have a limited carbonation level. Our novel design of customized biochar and CO2 curing could compensate for the strength deficiency of biochar-cement composites and extend the emerging applications of porous biochar in the cementitious composites for low-carbon construction.

Carbonation-enhanced Interfacial Transition Zone in Biochar-Cement Mortar