Anchoring Platinum Clusters onto Oxygen Vacancy-Modified In 2 O 3 for Ultraefficient, Low-Temperature, Highly Sensitive, and Stable Detection of Formaldehyde
Yucheng Ou,Gangqiang Zhu,Peng Liu,Yanmin Jia,Lujun Zhu,Junli Nie,Shaolin Zhang,Weibin Zhang,Jianzhi Gao,Hongbing Lu,Yu Huang,Xianjin Shi,Mirabbos Hojamberdiev
DOI: https://doi.org/10.1021/acssensors.2c00334
IF: 8.9
2022-04-01
ACS Sensors
Abstract:To avoid carcinogenicity, formaldehyde gas, currently being only detected at higher operating temperatures, should be selectively detected in time with ppb concentration sensitivity in a room-temperature indoor environment. This is achieved in this work through introducing oxygen vacancies and Pt clusters on the surface of In2O3 to reduce the optimal operating temperature from 120 to 40 °C. Previous studies have shown that only water participates in the competitive adsorption on the sensor surface. Here, we experimentally confirm that the adsorbed water on the fabricated sensor surface is consumed via a chemical reaction due to the strong interaction between the oxygen vacancies and Pt clusters. Therefore, the long-term stability of formaldehyde gas detection is improved. The results of theoretical calculations in this work reveal that the excellent formaldehyde gas detection of Pt/In2O3–x originates from the electron enrichment due to the surface oxygen vacancies and the molecular adsorption and activation ability of Pt clusters on the surface. The developed Pt/In2O3–x sensor has potential use in the ultraefficient, low-temperature, highly sensitive, and stable detection of indoor formaldehyde at an operating temperature as low as room temperature.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssensors.2c00334.Synthetic methods of In2O3, In2, and Pt/In2O3–x; gas-sensing experiments and DFT calculations; XRD patterns of In2O3, In2O3–x, and Pt/In2O3–x; N2 adsorption–desorption isotherms and corresponding pore-size distribution curves of In2O3, In2O3–x, and Pt/In2O3–x; SEM images of In2O3, In2O3–x, and Pt/In2O3–x; HAADF-STEM images of Pt/In2O3; HAADF-STEM images of In2O3; HAADF-STEM images of In2O3–x, ABF-STEM images of In2O3–x, magnified area of the region, and intensity profile corresponding to the yellow dashed line; In 3d, O 1s, and Pt 4f high-resolution XPS spectra of In2O3, In2O3–x, and Pt/In2O3–x before and after the reaction; EPR spectrum of In2O3–x; response time of the In2O3 sensor in 100 ppm HCHO at different temperatures; response time of the In2O3–x sensor in 100 ppm HCHO at different temperatures; response time of the Pt/In2O3–x sensor in 100 ppm HCHO at different temperatures; dynamic sensing transient curves for different HCHO concentrations of In2O3, In2O3–x, and Pt/In2O3–x at optimum working temperature; DMPO spin-trapping ESR spectrum of Pt/In2O3–x for O–; structure models and adsorption energies for various gases of In2O3, In2O3–x, and Pt/In2O3–x; gas-sensing reproducibility of In2O3, In2O3–x, and Pt/In2O3–x sensors at an optimum working temperature; dynamic sensing transient curves for different concentrations of HCHO of In2O3–x and Pt/In2O3–x sensors at room temperature; gas-sensing reproducibility of In2O3, In2O3–x, and Pt/In2O3–x sensors at room temperature; dynamic sensing transient curves for low concentration of HCHO of Pt/In2O3–x; corresponding log(Sg–1) versus log(Cg) curves and response–recovery times of In2O3–x and Pt/In2O3–x sensors at room temperature; selectivity of In2O3, In2O3–x, and Pt/In2O3–x sensors at room temperature; DOS and PDOS of In2O3, In2O3–x, and Pt/In2O3–x sensors before and after the adsorption of oxygen and formaldehyde; structural models and adsorption energies for water molecules, oxygen, and formaldehyde of In2O3, In2O3–x, and Pt/In2O3–x; corresponding mapping of in situ FTIR spectra: gas-sensing reaction on the -Abstract Truncated-
chemistry, multidisciplinary, analytical,nanoscience & nanotechnology