A Novel Dissimilar Resistance Spot Welding of Ti6Al4V Alloy and 316L Stainless Steel Via Copper As Interlayer by Using Optimal Electrodes

Weihua Zhang,Kunlong Zhang,Yue Yang,Xiangyu Sun,Sirong Yu,Yongqiang Li,Yongtao Yu,Daqian Sun

DOI: https://doi.org/10.1016/j.jmrt.2024.10.183

2024-01-01

Abstract:A novel dissimilar resistance spot welding of Ti6Al4V alloy and 316L stainless steel was performed via copper as interlayer by using optimal electrodes. A significant improvement in nugget morphology being of less defects was achieved with increasing the copper interlayer thickness from 50 mu m to 400 mu m. Thinner interfacial reaction layers at both the nugget/titanium interface and the nugget/stainless steel interface and finer equiaxed dendritic grained structure at the inner nugget were formed with copper interlayer thickness of 300 mu m compared with those without interlayer. The formation of TiCu and Ti2Cu was facilitated with the incorporation of Cu into the nugget, which effectively inhibited the formation of the brittle Ti-Fe intermetallic compounds including Fe2Ti. The nugget in the welded joint with copper interlayer in 300 mu m thickness exhibited a far lower microhardness than that of the interlayer-free welded joint, and the average microhardness reduced to 604 HV in the inner nugget, which was about 36% lower than that of the interlayer-free welded joint. The tensile shear load of the welded joint exhibited an increased tendency with increasing interlayer thicknesses from 50 mu m to 300 mu m, and the maximum tensile shear load of 6.3 kN was obtained with the interlayer thickness of 300 mu m, which was similar to 97% higher than that of the interlayer-free welded joint. The welded joint with copper interlayer exhibited hybrid ductile and fragile fractured characteristics. The work would provide a facile and cost-effective method to achieve a reliable welded joint of Ti alloy and stainless steel.