Abstract:The TC21 alloy has been extensively utilized in the aerospace structural components, making it crucial to investigate the fatigue damage mechanism of this alloy. In this study, a comprehensive investigation was conducted into the high-cycle fatigue damage mechanism of TC21 alloy under rotation bending, considering variations in primary equiaxed alpha (alpha p) phase contents and size in bimodal microstructure (BM). Results demonstrate that the TC21 alloy exhibits optimal strength-ductility and fatigue life at approximately 25 percent of the alpha p phase content. The content and dimension of the alpha p phase play a significant role in regulating the onset of fatigue fractures. Dislocation pile-up around the alpha p phase promotes the formation of microvoids and microcracks. Notably, when the content of the alpha p phase falls below 15 %, there is an increased influence from secondary alpha phase (alpha s) on crack initiation. Moreover, excessive amounts of alpha p coupled with decreased size lead to a reduction in fatigue life. The aforementioned factors contribute to an intensified concentration of stress, facilitate a more uniform path for crack extension, and expedite the rate of fatigue crack propagation.

Rotation Bending High Cycle Fatigue Behaviors of TC21 Alloy with Bimodal Microstructure