Preparation of V2O5 Using Pb5(VO4)3OH Recovered from Bayer Vanadium Sludge Through H2SO4 Pre-Treatment, H2O2 Leaching, V5O12•6H2O and V10O24•12H2O Precipitation and Oxidative Roasting at 400 °C

Changda Zhang,Qiusheng Zhou,Yilin Wang,Leiting Shen,Guihua Liu,Tiangui Qi,Zhihong Peng,Xiaobin Li

DOI: https://doi.org/10.1016/j.hydromet.2024.106404

IF: 4.217

2025-01-01

Hydrometallurgy

Abstract:Bayer vanadium sludge (BVS), discharged during the Bayer alumina production, is a promising secondary resource for the supply of vanadium. Previous vanadium extraction process involving Pb-5(VO4)(3)OH precipitation by PbSO4, H2SO4 and (NH4)(2)SO3 leaching, (NH4)(2)S2O8 oxidation followed by ammonium vanadate precipitation, suffered from large amounts of reagent consumption and discharge of ammonia-containing waste. In this study, a cleaner and cost-efficient process based on H2SO4 pre-treatment, H2O2 leaching, hydrolytic precipitation, and preparation of V2O5 through oxidative roasting was proposed to reduce reagent consumption and waste. Results show that the maximum vanadium leaching efficiency reached 99.7 % under the most suitable conditions of H2SO4 pre-treatment with H2SO4/Pb-5(VO4)(3)OH molar ratio of 6.5, pulp density of 250 g/L at 90 degrees C for 4 h followed by H2O2 leaching with H2O2/V molar ratio of 3.0 at 15 degrees C for 10 min. Furthermore, 96.5 % of vanadium was precipitated in the forms of V5O12 center dot 6H(2)O and V10O24 center dot 12H(2)O by heating the leach liquors to 100 degrees C for 60 min, followed by the oxidative roasting at 400 degrees C for 2 h to prepare V2O5 product with a purity of 99.2 %, with only H2O as a by-product. This research provides new insights into vanadium extraction in a cleaner, cost-efficient, and sustainable industrial process which saves 147.4 $/t Pb-5(VO4)(3)OH.