Induction of Brand New Na3 Sites Constructing High Performance Na3V2(PO4)3 with Low Strain Property and High Thermal Safety

Yuru Zhao,Changcheng Liu,Que Huang,Hongyuan Ding,Jianghui Xie,Baofeng Zhang,Yanjun Chen

DOI: https://doi.org/10.1016/j.cej.2024.156605

IF: 15.1

2024-01-01

Chemical Engineering Journal

Abstract:The inert Na1 site of Na3V2(PO4)3 3 V 2 (PO 4 ) 3 (NVP) leads to poor capacities, which seriously hinders its further application. Herein, Na site regulation is initiatively explored by introducing Mg2+ 2 + into Na+ + site in NVP bulk. Rietveld XRD refinement with low R values demonstrates the successful occupancy of Na1 (16b) site by Mg2+. 2 + . Furthermore, Na-NMR testing of the modified Na2.96Mg0.02V2(PO4)3@5%CNTs 2.96 Mg 0.02 V 2 (PO 4 ) 3 @5%CNTs (NVP/C@Mg-2 %) indicates that additional active Na+ + sites at 12c rather than 16b and 18e for traditional Na1 and Na2 sites is generated in the crystal structure after introducing Mg2+. 2 + . The newly induced Na3 site can provide extra space for the reversible de- intercalation of Na+, + , which results in the effectively improved electrochemical capacity and kinetic characteristics. In addition, the doping of Mg2+ 2 + with a smaller radius is favourable to reduce the lattice strain because of the enlarged internal interspace, constructing a solid structural framework to maintain excellent cyclic stability, which has been demonstrated by ex-situ XRD measurement. Moreover, NVP/C@Mg-2 % possesses a honeycomb morphological structure with homogeneous pores, providing enough room for the volume shrinkage of electrode and benefiting for the infiltration of electrolyte. Accordingly, NVP/C@Mg-2 % delivers 98.3 mAh/g at 30C and maintains a value of 81.5 mAh/g after 2000 cycles, indicating superior rate performance and cyclic stability. Besides, after-cycled XRD/SEM/XPS verify the stable crystal structure for NVP/C@Mg-2 %. ARC test further manifests NVP/C@Mg-2 % behaves excellent thermal safety and stability with higher self-exothermic temperature.