Hemicellulose Bio-Based Films Via Crosslinking with Citric Acid and Its Preservation Effect on Chilies

Liyan Ma,Jiahui Shi,Shan Yang,Peng Lu,Rina Wu
DOI: https://doi.org/10.1016/j.indcrop.2024.119794
IF: 6.449
2024-01-01
Industrial Crops and Products
Abstract:As a prospective replacement for petroleum-based plastics in the packaging industry, bio-based films have attracted significant interest. Hemicellulose produced as a byproduct during the manufacture of dissolving pulp was utilized to fabricate films for high-value utilization. Citric acid (CA) was employed as green crosslinking agent to enhance intermolecular interactions to form a network structure for improved strength. Excessive CA might also act as plasticizer to improve the mechanical properties of the films. The prepared film showed moderate strength (51.07 MPa for C1-5 film) and good flexibility (elongation at break 89.63 % for C1-20 film) due to the effect of CA. Good oxygen (5.78 cm3 3 mu m m- 2 d- 1 KPa- 1 for C2-5 film) and water vapor (0.4 g mm m- 2 day- 1 KPa-- 1 for C1-20 film) barrier properties could also be obtained. Water resistance of the film was also enhanced through crosslinking indicated by increased water contact angle. Thanks to its good barrier ability, the obtained film exhibited capability in chili preservation. When wrapped with C1-5 film, color change and texture deterioration of chili could be effectively inhibited with reduced weight loss (26.22 %) after 7 days of storage.
What problem does this paper attempt to address?