Interfacial Modification of NiSe by Controllable Nanoscale Amorphous Phase Fe(OH)3 Layers to Achieve Efficient Water-Splitting Performance

Hezeng Xu,Yanling Qiu,Aowei Sun,Fuguang Liu,Yujia He,Jiangtao Xu,Jingquan Liu

DOI: https://doi.org/10.1016/j.ijhydene.2024.09.451

IF: 7.2

2024-01-01

International Journal of Hydrogen Energy

Abstract:In this study, we utilized interfacial engineering to modify the surface interface of the material via interfacial hydrolysis reaction at room temperature to establish a meticulously controllable micro-nanoscale amorphous hydroxide active layer, which serves as a cost-effective and highly efficient bifunctional electrocatalyst with remarkable catalytic activity and robust stability. We selected Fe(NO3)3 center dot 9H2O to induce the formation of amorphous Fe(OH)3 layer with different thicknesse on the surface of NiSe/NF by adjusting the Fe3+ concentrations, thereby exposing additional active sites on the NiSe@FeOH/NF-C50 surface. Moreover, the incorporation of Se not only augments the chemical stability of NiSe but also significantly enhances the charge transfer efficiency between NiSe and Fe(OH)s, while simultaneously improves interfacial stability. The synergistic effect between Ni and Fe significantly enhances the electron transfer rate, enabling the modified NiSe@FeOH/NF-C50 sample to exhibit outstanding OER/HER activity in 1 M KOH with current densities of 100 mA cm- 2 at OER and HER overpotentials of 260 mV and 253.2 mV, and with low Tafel slopes of 56.9 mV center dot dec- 1 and 85.7 mV center dot dec- 1, respectively. When the NiSe@FeOH/NF-C50 is employed as a bifunctional catalyst for an alkaline electrolyzed electrode, requires a low cell voltage of 1.776 V to produce 50 mA cm- 2 current density. Notably, the catalyst exhibits excellent stability over 60 h at 1.0 M KOH, underscoring its significant potential in commercial applications.