Electrochemical and Spectro-Microscopic Analyses of Charge Accumulation and Ion Migration in Dry Processed Perovskite Solar Cells under Electrical Biasing

Sufal Swaraj,Haeyeon Jun,Denis Tondelier,Bernard Geffroy,Ileana Florea,Jean‐Eric Bouree,Pilar Lopez-Varo,Philip Schulz,Yvan Bonnassieux

DOI: https://doi.org/10.26434/chemrxiv-2024-mgq6l

2024-10-01

Abstract:We study the influence of the electrical biasing on the modification of the chemical composition and the electrical performance of perovskite solar cells (PSCs) by coupling Electrochemical impedance spectroscopy (EIS) and scanning transmission X-ray microscopy (STXM) techniques. EIS reveals the formation of charge accumulation at the interfaces and changes in resistive and capacitive properties. STXM study on PSCs after applying strong electric field for a long biasing time indicates the break-down of methylammonium (MA+) cation promoting iodide ions to migrate and create defects at the interface. This complementary EIS and STXM study allows to suggest a degradation mechanism that includes the migration of iodide ions that leads to interface defects and subsequent degradation of solar cell performance. In addition, we study the evolution of the performance of PSCs under air. We observe an increased hysteresis index on current-voltage curves and fill factor reduction of the perovskite solar cells with ageing in air. EIS measurements show the formation of a capacitive layer resulting from accumulation of iodide ions through modification of the mobile ion concentration and ion mobility.

Chemistry

What problem does this paper attempt to address?

The paper aims to study the impact of electric bias on the chemical composition and electrical performance of perovskite solar cells (PSCs). Specifically, the authors explore the phenomena of charge accumulation and ion migration in perovskite solar cells under the influence of electric bias by combining electrochemical impedance spectroscopy (EIS) and scanning transmission X-ray microscopy (STXM) techniques. The paper focuses on how the decomposition of methylammonium (MA+) cations and the migration of iodide ions (I-) lead to interface defects, thereby affecting the performance of the cells. Additionally, the study investigates the aging process of these cells in air, observing an increase in the hysteresis index of the current-voltage curve and a decrease in the fill factor.

In short, the issues this study attempts to address include:
1. **The impact of electric bias on the performance of perovskite solar cells**: Specifically, how electric bias leads to changes in charge accumulation, resistance, and capacitance properties.
2. **Ion migration mechanisms**: Observing the migration paths of iodide ions and their impact on cell performance through STXM technology.
3. **Cell aging issues**: Studying the aging process of perovskite solar cells in air, particularly the specific effects of aging on cell performance.

These studies contribute to a deeper understanding of the stability and performance degradation mechanisms of perovskite solar cells in practical applications, providing important theoretical foundations and technical support for improving their long-term stability and efficiency.