RuO2/MnO2 Nanorods As High Efficient Electrocatalyst of Lithium-Oxygen Battery
Yue-Feng Xu,Gui‐Liang Xu,Xiaoru Zhang,Yuan Chen,Zonghai Chen,Ling Huang,Jun‐Tao Li,Khalil Amine,Shi‐Gang Sun
DOI: https://doi.org/10.1149/ma2016-02/5/810
2016-01-01
Abstract:Electrocatalyst is the key component in Li-O 2 batteries and attracted extensive attention in recent years. It has demonstrated that carbon materials 1 , transitional metal oxides 2 , noble metals 3 , and Perovskite-type oxides 4 can present high catalytic activity in oxygen reduction reaction (ORR) or in oxygen evolution reaction (OER) to facilitate decomposition of Li 2 O 2 . In order to explore high efficient electrocatalyst, in the present work, RuO 2 /MnO 2 nanorods were synthesized via a facile two-step hydrothermal reaction. Li-O 2 battery testing results demonstrated that the as-synthesized RuO 2 /MnO 2 nanorods exhibit excellent properties as electrocatalyst of oxygen cathode. The RuO 2 /MnO 2 nanorods could maintain a reversible capacity of 500 mAh g -1 in 75 cycles at a rate of 50mA g -1 , and a higher capacity of 4000 mAh g -1 in 20 cycles at a rate of 200mA g -1 . Moreover, the RuO 2 /MnO 2 nanorods present a much lower voltage polarization in charge/discharge processes than MnO 2 nanorods electrode does. The catalytic activities of RuO 2 /MnO 2 nanorods and MnO 2 nanorods were also compared by studies of rotating disk electrode (RDE). Furthermore, in situ high-energy X-ray diffraction and ex situ SEM were carried out to investigate the formation and decomposition of the discharge products Li 2 O 2 . Figure 1. (a)(b) In-situ XRD patterns of the electrode in discharge process for 20 h. (c) Charge/discharge curves of RuO 2 /MnO 2 nanorods at a rate of 50 mA g -1 . ACKNOWLEDGMENT: This work was financially supported by NSFC (Grant Nos. 21373008, 21321062, 21273184) REFERENCES: (1) Liu, T.; Leskes, M.; Yu, W.; Moore, A. J.; Zhou, L.; Bayley, P. M.; Kim, G.; Grey, C. P., Science 2015, 350, 530-533. (2) Zhang, P.; Sun, D.; He, M.; Lang, J.; Xu, S.; Yan, X., ChemSusChem 2015, 8, 1972-1979. (3) Bruce, P. G., Science 2012, 337, 563-566. (4) Xu, J. J.; Xu, D.; Wang, Z. L.; Wang, H. G.; Zhang, L. L.; Zhang, X. B., Angewandte Chemie 2013, 52, 3887-90. Figure 1