Flexible MOF on CoxFe1-xOOH@Biomass Derived Alloy@Carbon Films for Efficient Electromagnetic Interference Shielding and Energy Conversion
Wenhao Bai,Jianyu Zhai,Shengguo Zhou,Ce Cui,Weijie Wang,Shan Jiang,Cheng,Erhui Ren,Hongyan Xiao,Mi Zhou,Jinwei Zhang,Ronghui Guo
DOI: https://doi.org/10.1016/j.carbon.2022.07.059
IF: 10.9
2022-01-01
Carbon
Abstract:Increasingly serious electromagnetic pollution makes efficient electromagnetic shielding more important. Herein, the CoxFe1-xOOH nanoneedles were creatively synthesized by hydrothermal method and firmly anchored on cotton fabric. Subsequently, CoFe/CoCu-PDMS-carbon films (CoFe/CoCu-PCFs) were prepared by in-situ growth CoCu MOF along CoxFe1-xOOH nanoneedles, annealing, encapsulating by diluted PDMS. CoxFe1-xOOH derived interlinked CoFe alloy conductive network. 2D leaf-like CoCu MOF nanosheets grow along 1D CoxFe1-xOOH nanoneedles, forming a unique "leaf-branch" protection mechanism to inhibit the shrink of composites. Intertwined CoFe/CoCu alloy-carbon fiber with skin-core structure forms double conductive network, which reduces the density and strengthens the absorption during multiple reflection of electromagnetic waves. As results, CoFe/CoCu-PCF-45 (CoCu MOF growing for 45 min) shows the average electromagnetic interference shielding efficiency (EMI SE), SE/t (thickness) and SSE (SE/density)/t reaching 73.46 dB, 3296.62 dB/cm and 12227.21 dB cm(2) g(-1) , respectively. CoFe/CoCu-PCF-45 maintains high-level shielding performance (>60 dB) after bending 600 cycles at 90 degrees, ultrasonic damage for 3 h and acid/alkali/salt corrosion for 12 h. In addition, CoFe/CoCu-PCF-45 possesses efficient, fast and stable energy conversion (over 150 degrees C in 10 s at 0.8 V voltage, over 70 degrees C in 3 s at 0.3 W cm(-2) illumination intensity). This work provides new ideas for designing efficient EMI shielding composites.