Interface Characteristics and Tribological Properties of Laser Cladded FeCoCrNiAl0.5Ti0.5 Coating on AISI1045 Steel
CAO Jiajun,CHANG Cheng,QIU Zhaoguo,ZENG Dechang,LIU Min,YAN Xingchen
DOI: https://doi.org/10.11933/j.issn.1007-9289.20220524002
2023-01-01
China surface engineering
Abstract:AISI 1045 steel has good workability and exceptional comprehensive mechanical properties due to hardening and tempering, relying on a tempered sorbitic matrix. However, it is vulnerable to wear even after heat treatment when used in load-bearing applications. An appropriate fabrication method is urgently required to strengthen the surface properties of AISI 1045 steel. Laser cladding（LC）, an advanced surface modification technique, has become a research hotspot owing to its adjustable processing parameters, ultrafast heating/cooling rate, and utilization of high-energy beams. It provides a method for the preparation of high-entropy alloy（HEAs） coatings on the surface of AISI 1045 steel to increase the surface wear resistance and hardness.Benefiting from the characteristics of HEAs and the merits of the LC process, the dense HEAs coating fabricated by LC has good metallurgical bonding on the substrate and generates a small amount of precipitation, such as intermetallic compounds, to strengthen the coating. At present, research on the wear of laser-cladding high-entropy alloy coatings mainly focuses on the coating surface, and the tribological behavior of the coating/substrate interface region has rarely been studied. A series of FeCoCrNiAl 0.5 Ti 0.5 coatings with good macromorphology and uniform microstructure were fabricated on an AISI 1045 steel substrate using laser cladding technology to improve the wear resistance of AISI 1045 steel. The microstructure and phase distribution were investigated by optical microscope（OM）, X-ray diffraction（XRD）, scanning electron microscope（SEM）, and energy dispersive spectroscopy（EDS）. The coating consists of planar crystals, columnar dendrite crystals, and equiaxed crystals from the bottom to the top. The XRD pattern and elemental distribution of the FeCoCrNiAl 0.5 Ti 0.5 coatings revealed that the coating was composed of a eutectic structure face-centered cubic phase（Fe, Ni）, some body-centered cubic phase（BCC） and dispersed NiAl intermetallic compounds. In addition, hardening phases such as Cr23C6 and CoTi2 are formed when carbon is dissolved in the coating/substrate interface region, and the substrate is composed of fine lath martensite α’-（Cr, Fe）. The microhardness and tribological properties of the coatings were tested using a Vickers hardness tester and a tribometer. From the top of the coatings to the substrate, the average microhardness of the coating,dilution area, heat-affected zone, and substrate were 518±20 HV0.2, 561±63 HV0.2, 473±81 HV0.2 and 217±12HV0.2, respectively.This shows a trend of first increasing and then decreasing due to the deposition of Cr 23 C 6 in the dilution area and the depression of the quenching effect on the substrate. The wear tests showed that the mechanisms were abrasive wear on the substrate, a combination of adhesive and oxidative wear on the coating, and a combination of abrasive and oxidative wear on the coating/substrate interface region. During friction, the substrate produces a large amount of spalling and oxidation debris, followed by severe three-body wear.The coating formed a cycle of oxide film growth-crack-detaching, causing coating wear. Compared with the coating and substrate, the Cr 23 C 6 and friction layer are formed in the coating/substrate interface region during the friction process to protect the interface region,which provides a theoretical reference for the tribological behavior of the coating/interface region. The coefficient of friction on the coating/substrate interface region（COF=0.56） and the wear rate(4.76±0.51×10 -5 mm~3/（N·m）) were the lowest. The wear rate of the coating/substrate interface region is half that of the substrate, which is slightly lower than that of the coating.