Abstract:Zinc (Zn) and some of its alloys are recognized as promising biodegradable implant materials due to their acceptable biocompatibility, facile processability, and moderate degradation rate. Nevertheless, the limited mechanical properties and stability of as-cast Zn alloys hinder their clinical application. In this work, hot-rolled (HR) and hot-extruded (HE) Zn-5 wt.% gadolinium (Zn-5Gd) samples were prepared by casting and respectively combining with hot rolling and hot extrusion for bone-implant applications. Their microstructure evolution, mechanical properties, corrosion behavior, cytotoxicity, antibacterial ability, and in vitro and in vivo osteogenesis were systematically evaluated. The HR and HE Zn-5Gd exhibited significantly improved mechanical properties compared with those of their pure Zn counterparts and the HR Zn-5Gd showed a unique combination of tensile properties with an ultimate tensile strength of ∼311.6 MPa, yield strength of ∼236.5 MPa, and elongation of ∼40.6%, all of which are greater than the mechanical properties required for bone-implant materials. The HR and HE Zn-5Gd showed higher corrosion resistance than their pure Zn counterpart in Hanks' solution and the HE Zn-5Gd had the lowest corrosion rate of 155 μm/y measured by electrochemical corrosion and degradation rate of 26.9 μm/y measured by immersion testing. The HR and HE Zn-5Gd showed high cytocompatibility toward MC3T3-E1 and MG-63 cells, high antibacterial effects against S. aureus , and better in vitro osteogenic activity than their pure Zn counterparts. Furthermore, the HE Zn-5Gd exhibited better in vivo biocompatibility, osteogenesis, and osteointegration ability than pure Zn and pure Ti. Statement of significance This work reports the mechanical properties, corrosion behaviors, cytocompatibility, antibacterial ability, in vitro and in vivo osteogenesis of biodegradable Zn–Gd alloy for bone-implant applications. Our findings demonstrate that the hot-rolled (HR) Zn–5Gd showed a unique combination of tensile properties with an ultimate tensile strength of ∼311.6 MPa, yield strength of ∼236.5 MPa, and elongation of ∼40.6%. The HR and HE Zn-5Gd showed higher corrosion resistance than their pure Zn counterpart in Hanks' solution. The HR and HE Zn-5Gd showed high cytocompatibility toward MC3T3-E1 and MG-63 cells, good antibacterial effects against S. aureus , and better in vitro osteogenic activity. Furthermore, the HE Zn-5Gd exhibited better in vivo biocompatibility, osteogenesis, and osteointegration ability than pure Zn and pure Ti.

Improved Mechanical and Corrosion Properties Through High-Pressure Phase Transition in a Biodegradable Zn-1.5Mn Alloy

Optimization of Mechanical, Corrosion Properties and Cytotoxicity of Biodegradable Zn-Mn Alloys by Synergy of High-Pressure Solidification and Cold Rolling Process

Micro-alloying with Mn in Zn–Mg alloy for future biodegradable metals application

<i>In vitro</i> and <i>in vivo</i> studies of Zn-Mn biodegradable metals designed for orthopedic applications

Ultrahigh Strength and Uniform Corrosion in Zn-Li Alloys Through Ultrahigh Pressure Supersaturated Solid Solution Treatment for Biodegradable Orthopedic Applications

Biodegradable Zn-Mn Alloys with Suitable Mechanical Strength, High Plasticity, and Good Osteogenic Activities for Orthopedic Applications

Microstructure and properties of biodegradable Zn-0.8Mn-0.5Cu-0.2Sr alloys processed by ECAP

An in vitro and in vivo study of biodegradable Zn–Cu–Li alloy with high strength and ductility fabricated by hot extrusion combined with room-temperature ECAP

Microstructure and mechanical properties of biodegradable Zn-2Cu-0.1Ti alloy for orthopedic applications

Influence of Sr and Mn elements on the microstructural characteristics, mechanical and anti‐corrosion properties of Zn‐based biodegradable materials

Biodegradable Zn-Cu-Mn alloy with suitable mechanical performance and in vitro degradation behavior as a promising candidate for vascular stents

Enhanced Mechanical Performance and Tailored Degradation Characteristics of Rolled Zn-0.8Li-0.4Mn Alloy

Preparing High Strength and Elongation of Biodegradable Zinc–Magnesium Alloys with Superior Antibacterial Properties and Biocompatibility

Enhanced Mechanical Properties, Corrosion Resistance, Cytocompatibility, Osteogenesis, and Antibacterial Performance of Biodegradable Mg‐2Zn‐0.5Ca‐0.5Sr/Zr Alloys for Bone‐Implant Application

Development of Biomedical Ti-Nb-Zr-Mn Alloys with Enhanced Mechanical Properties and Corrosion Resistance

Impact of copper on corrosion behavior, biocompatibility and antibaterial activity of biodegradable Zn-3Mg-xCu alloys for orthopedic applications

Investigation of Biodegradable Zinc-Based Alloy with Varying Compositions of Aluminum and Copper for Orthopedic Applications

Microstructure, Mechanical Properties, Corrosion Behavior and Biocompatibility of As-Extruded Biodegradable Mg–3Sn–1Zn–0.5Mn Alloy

A biodegradable Zn-5Gd alloy with biomechanical compatibility, cytocompatibility, antibacterial ability, and in vitro and in vivo osteogenesis for orthopedic applications

Design and characterizations of novel biodegradable Zn-Cu-Mg alloys for potential biodegradable implants

Mechanical Strength, Biodegradation, and In Vitro and In Vivo Biocompatibility of Zn Biomaterials.