Color‐tunable and White Emission of Tm3+ Doped Transparent Zinc Silicate Glass‐ceramics Embedding ZnO Nanocrystals
Jing Zhou,Bin Song,Huijun Qin,Wangwei Lu,Gaoling Zhao,Zhongping Huang,Gaorong Han
DOI: https://doi.org/10.1111/jace.16775
IF: 4.186
2019-01-01
Journal of the American Ceramic Society
Abstract:Tm3+ doped zinc silicate glass-ceramics composed of SiO2-Al2O3-ZnO-K2O-Tm2O3 embedded with ZnO nanocrystals were successfully fabricated by melt-quenching method with subsequent heat treatment. Tm3+ ions and ZnO nanocrystals were introduced as blue and yellow luminescence centers, respectively. The effects of heat treatment, excitation wavelength and Tm3+ doping concentration on the photoluminescence behaviors of these glass-ceramics were studied. Short-time (5 minutes) heat treatment was considered as the optimal heat treatment time, which facilitates simultaneously emitting narrow blue peak located at 453 nm and a broad yellow band centered at 580 nm. Blue and yellow emissions could be attributed to the D-1(2) -> F-3(4) transition of Tm3+ and Zn-i/O-i-related defect emission of ZnO nanocrystals, respectively. The combination of these two emissions allows the realization of white light emitting in the glass-ceramic samples. Furthermore, tunable luminescent color and chromaticity coordinates, including yellow, white and blue, can be realized by varying the pumping wavelengths as well as the content of Tm3+ dopant in the glass matrix. Nearly perfect white light emission with Commission Internationale de l'Eclairage coordinate (x = 0.33, y = 0.32) was achieved for the 0.05 mol% Tm3+ doped glass-ceramic embedding ZnO nanocrystals by heat treatment at 750 degrees C for 5 minutes under the excitation of 360 nm. These luminescent glass-ceramics doped with Tm3+ ion and ZnO nanocrystals could be a promising candidate for white light emitting devices under near-ultraviolet excitation.