Abstract:Manganese oxides with varied Mn valance states but identical morphologies were synthesized via a facile thermal treatment of γ-MnOOH. Also, their catalytic performance on ozone decomposition was investigated following the order of Mn3O4 < Mn2O3 < MnO2 < MnO2-H-200. In combination with X-ray diffraction (XRD), scanning electron microscopy (SEM), Brunauer–Emmett–Teller (BET), transmission electron microscopy (TEM), H2-temperature-programmed reduction (TPR), O2-temperature-programmed desorption (TPD), and X-ray photoelectron spectroscopy (XPS) characterization, it was deduced that the superior O3 decomposition capacity for MnO2-H-200 was strongly associated with abundant oxygen vacancies on its surface. Among Mn3O4, Mn2O3, and MnO2, the difference in O3 decomposition efficiency was dependent on the divergent nature of oxygen vacancy. Density functional theory (DFT) calculation revealed that Mn3O4 and MnO2 possessed lower formation energy of oxygen vacancy, while MnO2 had the minimum desorption energy of peroxide species (O2*). It was deduced that the promotion of the O3 decomposition capability was attributed to the easier O2* desorption. Insights into the deactivation mechanism for MnO2-H-200 further validated the assumptions. As the reaction proceeded, adsorbed oxygen species accumulated on the catalyst surface, and a portion of them were transformed to lattice oxygen. The consumption of oxygen vacancy led to the deactivation of the catalyst.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.langmuir.0c02841?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.langmuir.0c02841</a>.Catalyst preparation; catalyst characterization; XRD patterns of the as-prepared γ-MnOOH; N2 adsorption and desorption isotherms of different MnOx catalysts; top plane view and the oxygen vacancy sites of the preferentially exposed crystal plane for various MnOx during DFT calculation; FT-IR spectra of MnO2-H-200 and partially deactivate MnO2-H-200 catalysts; ozone conversion over MnO2-H-200 and the regenerated MnO2-H-200; the pore size distribution of different MnOx catalysts calculated by the BJH method (<a class="ext-link" href="/doi/suppl/10.1021/acs.langmuir.0c02841/suppl_file/la0c02841_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Efficient Ozone Decomposition by Amorphous Mn–Ni Bimetallic Catalysts under an Entire Humidity Environment

Efficient ozone decomposition over nickel-modified amorphous MnOx catalysts

Efficient Ozone Decomposition over Nickel-Modified Amorphous MnO X Catalysts

Efficient Ozone Decomposition by Optimizing Defect Sites of NiMn-layered Double Hydroxides under High Humidity Air

Highly Efficient Ozone Decomposition Against Harsh Environments over Long-Term Stable Amorphous MnOx Catalysts

Highly efficient removal of ozone by amorphous manganese oxides synthesized with a simple hydrothermal method

Effect of different structure of Cu/Mn catalysts on ozone decomposition ability

A superior catalyst for ozone decomposition: NiFe layered double hydroxide

Catalysts for Highly Water-Resistant Catalytic Decomposition of Ozone: Hausmannite Mn3O4 on Exposed (101) Crystal Surface.

Enhancing ozone catalytic decomposition through acid treatment of α-MnO2 for improved activity and humidity resistance

Heterostructured Ni/NiO Nanocatalysts for Ozone Decomposition

Co-doped cryptomelane-type manganese oxide in situ grown on a nickel foam substrate for high humidity ozone decomposition

High Performance Ozone Decomposition over MnAl-based Mixed Oxide Catalysts Derived from Layered Double Hydroxides

Highly Efficient Removal of Ozone on Amorphous Manganese Oxides Modified by Alkali Metals

α-MnO 2 catalysts with efficient ozone-catalyzed decomposition under high humidity conditions

Efficient ozone decomposition over bifunctional Co3Mn-layered double hydroxide with strong electronic interaction

Facile Synthesis Of Amorphous Mesoporous Manganese Oxides For Efficient Catalytic Decomposition Of Ozone

Efficient monolithic MnOx catalyst prepared by heat treatment for ozone decomposition

Insights into the Reactive and Deactivation Mechanisms of Manganese Oxides for Ozone Elimination: The Roles of Surface Oxygen Species

Enhanced water-resistance of Mn-based catalysts for ambient temperature ozone elimination: Roles of N and Pd modification

Exceptional Ozone Decomposition over -MnO2/AC under an Entire Humidity Environment