High-temperature Creep Mechanism of Ti-Ta-Nb-Mo-Zr Refractory High-Entropy Alloys Prepared by Laser Powder Bed Fusion Technology

Junyi Feng,Binghao Wang,Yintao Zhang,Peilei Zhang,Changxi Liu,Xiaoli Ma,Kuaishe Wang,Lechun Xie,Ning Li,Liqiang Wang
DOI: https://doi.org/10.1016/j.ijplas.2024.104080
IF: 8.5
2024-01-01
International Journal of Plasticity
Abstract:Creep resistance, which is one of the most important deformation modes, is rarely reported for refractory high entropy alloys (RHEAs). The experiment investigated the high-temperature creep mechanism of Ti-Ta-Nb-Mo-Zr RHEA prepared by laser powder bed fusion (LPBF) technology. The high cooling rate of LPBF suppresses most of the elemental segregation, but there are still over-solidified precipitates and a few continuous precipitates (CP). In the range of 923-1023 K, the stress exponent and activation energy were determined to be 3.2-3.4 and 261.5 +/- 19.5 kJ/ mol, respectively. Compared with other conventional alloys and HEAs, a large reduction of the minimum creep rate is found in the LPBF-built Ti1.5Ta0.5NbZrMo0.5 RHEA, indicating a significant improvement in high-temperature properties. The dislocation tangles at the interface is formed during the creep process and new Zr-rich CP phases are generated in the dislocation tangles region. The interfacial dislocation tangles is the result of the interaction between dislocations and two-phase mismatch stresses. The dislocation tangles prevents dislocations from further cutting the matrix phase, which is very favorable to the high-temperature creep performance. At the same time, the formation of this dislocation tangles greatly accelerates the nucleation process and growth rate of the new CP phase. The present work provides a pathway to design novel HEAs with improved high-temperature creep resistance.
What problem does this paper attempt to address?