Abstract:For commercial applications, the need for smaller footprint energy storage devices requires more energy to be stored per unit area. Carbon nanomaterials, especially graphene, have been studied as supercapacitor electrodes and can achieve high gravimetric capacities affording high gravimetric energy densities. However, most nanocarbon-based electrodes exhibit a significant decrease in their areal capacitances when scaled to the high mass loadings typically used in commercially available cells (∼10 mg/cm2). One of the reasons for this behavior is that the additional surface area in thick electrodes is not readily accessible by electrolyte ions due to the large tortuosity. Furthermore, the fabrication of such electrodes often involves complicated processes that limit the potential for mass production. Here, holey graphene electrodes for supercapacitors that are scalable in both production and areal capacitance are presented. The lateral surface porosity on the graphene sheets was created using a facile single-step air oxidation method, and the resultant holey graphene was compacted under ambient conditions into mechanically robust monolithic shapes that can be directly used as binder-free electrodes. In comparison, pristine graphene discs under similar binder-free compression molding conditions were extremely brittle and thus not deemed useful for electrode applications. The coin cell supercapacitors, based on these holey graphene electrodes exhibited small variations in gravimetric capacitance over a wide range of areal mass loadings (∼1-30 mg/cm2) at current densities as high as 30 mA/cm2, resulting in the near-linear increase of the areal capacitance (F/cm2) with the mass loading. The prospects of the presented method for facile binder-free ultrathick graphene electrode fabrication are discussed.

Preparation and Supercapacitive Behaviors of the Porous Reduced Graphene Derived from the Graphite Anode of Spent Lithium-Ion Batteries

A Novel and Facile Synthesis Approach for a Porous Carbon/graphene Composite for High-Performance Supercapacitors

Enhanced Supercapacitor Performance Based on 3D Porous Graphene with MoO2 Nanoparticles

Preparation of Hierarchically Porous Carbon Nanosheet Composites with Graphene Conductive Scaffolds for Supercapacitors: an Electrostatic-Assistant Fabrication Strategy

High-Performance Supercapacitors Based on Graphene/Activated Carbon Hybrid Electrodes Prepared Via Dry Processing

Wet-spun, porous, orientational graphene hydrogel films for high-performance supercapacitor electrodes.

Facile Synthesis of Porous Graphene As Binder-Free Electrode for Supercapacitor Application

Electrospray-Deposition of Graphene Electrodes: A Simple Technique to Build High-Performance Supercapacitors

Interconnected Frameworks with a Sandwiched Porous Carbon Layer/Graphene Hybrids for Supercapacitors with High Gravimetric and Volumetric Performances

Preparation and properties of graphene for supercapacitor application

Fabrication and enhanced supercapacitive performance of sulfur and nitrogen co-doped porous graphene

Nickel Acetate-Assisted Graphitization of Porous Activated Carbon at Low Temperature for Supercapacitors With High Performances

3D porous oxygen-enriched graphene hydrogels with well-balanced volumetric and gravimetric performance for symmetric supercapacitors

A method for the preparation of graphene from spent graphite of retired lithium-ion batteries

Partially Graphitic Hierarchical Porous Carbon Nanofiber for High Performance Supercapacitors and Lithium Ion Batteries

Scalable Preparation of Hierarchical Porous Activated Carbon/graphene Composites for High-Performance Supercapacitors

Facile Preparation of Porous Carbons Derived from Orange Peel Via Basic Copper Carbonate Activation for Supercapacitors

Biomass-derived graphene-like carbon nanoflakes for advanced supercapacitor and hydrogen evolution reaction

Facile and low-cost fabrication of interconnected hierarchically porous carbon for high-performance supercapacitors

Dry-Processed, Binder-Free Holey Graphene Electrodes for Supercapacitors with Ultrahigh Areal Loadings.

In-situ Chemical Reduction Produced Graphene Paper for Flexible Supercapacitors with Impressive Capacitive Performance