Abstract:Photomultiplication-type polymer photodetectors (PM-PPDs) were fabricated with hole-only transport active layers containing polymer(s): [6,6]-phenylC61-butyric acid methyl ester (PC61BM) with a weight ratio of 100:2. The rather less PC61BM content in active layers prefers to generate a large amount of isolated electron traps surrounded by polymers. Photogenerated electrons prefer to be trapped by the isolated PC61BM due to the lack of continuous electron-transport channels. The trapped electrons by the isolated PC61BM close to the Al electrode would like to seduce hole tunneling injection. The transparent polymer poly[N,N′-bis(4-butylphenyl)-N,N′-bis(phenyl)benzidine] (poly-TPD) was incorporated as a regulator to improve hole mobility (μh) and adjust the trapped-electron distribution in active layers, leading to the enhanced performance of PM-PPDs. The optimal PM-PPDs were achieved using poly(3-hexylthiophene) (P3HT):poly-TPD:PC61BM (80:20:2, wt/wt/wt) as active layers. External quantum efficiency (EQE) values at 620 nm are 3900 and 1250% for PM-PPDs based on P3HT:poly-TPD:PC61BM (80:20:2, wt/wt/wt) and P3HT:PC61BM (100:2, wt/wt) under −10 V applied voltage, respectively. The EQE at 620 nm of optimal PM-PPDs is improved from 650 to 63,000% along with the applied voltage increase from −5 to −20 V. This work provides a new strategy of using transparent polymer with large μh as a regulator for EQE and response speed improvement, as well as the flattened EQE spectral shape of PM-PPDs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c06486?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c06486</a>.J–V curves of poly-TPD:PC61BM (100:1, wt/wt)-based devices, PL spectra of neat poly-TPD films and poly-TPD:PC61BM blend films, ln(Jd3/V2)–(V/d)1/2 curves, absorption spectra of P3HT:poly-TPD:PC61BM blend films with different poly-TPD contents, extinction coefficient and refractive index of P3HT:PC61BM (100:2, wt/wt) and P3HT:poly-TPD:PC61BM (80:20:2, wt/wt/wt) blend films, optical-field distribution in P3HT:PC61BM (100:2, wt/wt) and P3HT:poly-TPD:PC61BM (80:20:2, wt/wt/wt)-based PM-PPDs, and NEP spectrum of optimal PM-PPDs (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c06486/suppl_file/am1c06486_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Suppressing the Dark Current Density of Organic Photodetectors by Narrowing the Molecular Weight Distribution

Enhanced Detectivity of Organic Photodetectors with a Non-Conjugated Polymer Additive

Dark Current Reduction Strategy Via a Layer-By-Layer Solution Process for a High-Performance All-Polymer Photodetector

Achieving High-detectivity Near Infrared Organic Photodetectors through Optimizing Film Thickness and Polymer Molecular Weight

Optimization of Broad-Response and High-Detectivity Polymer Photodetectors by Bandgap Engineering of Weak Donor-Strong Acceptor Polymers

Photo-crosslinking and layer-by-layer processed organic photodetectors with remarkably suppressed dark current

Mitigating Dark Current and Improving Charge Collection for High-Performance Near-Infrared Organic Photodiodes Via P-Doping Strategy

Efficient All‐Polymer Photomultiplication‐Type Organic Photodetectors with Prolonged Crystallization Process

Diminished Trap-Induced Leakage Current at the Organic/Electrode Interface for High-Performance Organic Photodetectors

Enhanced Gain in Organic Photodetectors Using the Polymer with Singlet Open‐Shell Ground State

High-Performance Organic Phototransistors Based on D18, a High-Mobility and Unipolar Polymer

Enhanced Fibrillar Network and Molecular Crystallization via Volatile Solid Additives Enable Efficient Near‐Infrared Organic Photodetectors

Ultralow dark current in near-infrared organic photodetector via crosslinked conjugated polyelectrolyte hole-transporting layer

Optimization of Solubility, Film Morphology and Photodetector Performance by Molecular Side‐Chain Engineering of Low‐Bandgap Thienothiadiazole‐Based Polymers

Organic X‐Ray Image Sensors Using a Medium Bandgap Polymer Donor with Low Dark Current

Quantification of an Effective Charge Injection Barrier in Non-Fullerene-based Organic Photodetectors

Smart Strategy: Transparent Hole-Transporting Polymer as a Regulator to Optimize Photomultiplication-type Polymer Photodetectors

High-Performance All-Polymer Photodetectors Via a Thick Photoactive Layer Strategy

Enhanced molecular planarity for high-performance photodetectors: Effect of backbone conformation via alkyl substitution position control in dithienoquinoxaline-based conjugated polymers

Molecular Doping Increases the Semitransparent Photovoltaic Performance of Dilute Bulk Heterojunction Film with Discontinuous Polymer Donor Networks

2,1,3-Benzothiadiazole-5,6-dicarboxylic Imide Based Low-Bandgap Polymers for Solution Processed Photodiode Application