Abstract:In the trend of integration of structure and function, novel thermal management materials are urgent to be developed owning good mechanical properties as well as excellent thermal properties. In this work, a complete and dense copper (Cu) coating with a thickness of 400 nm was deposited on the surfaces of graphite films (GFs) by ultrasonic-assisted electroless plating, which can improve the surface roughness of GFs and interfacial bonding between GFs and Cu foils. Cu-coated and uncoated GFs reinforced copper matrix laminated composites (noted as GFs(Cu)/Cu and GFs/Cu) were fabricated by optimized vacuum hot-pressing sintering. Based on the scratch test and microstructures of GFs(Cu) and GFs(Cu)/Cu composites, addition of Cu coating can improve the interfacial adhesion and element diffusion behavior, and intuitively explains the mechanical interlocking effect at the C-Cu interface. On basis of the nanoindentation mechanical properties across GFs(Cu)/Cu and GFs/Cu interfaces, the interfacial transition region with Cu coating of similar to 3 mu m is three times of that without Cu coating. Flexural strength of 27.6 vol% GFs(Cu)/Cu laminated composite is 45.9 MPa, which is 56% higher than that of the corresponding GFs/Cu laminated composite. In-plane thermal conductivity (TC) and out-of-plane coefficient of thermal expansion (CTE) of 69.4 vol % GFs(Cu)/Cu laminated composite are 1177.8 W/mK and -2.5 ppm/K respectively, which could be explained on the theoretical calculations and interfacial structures. In conclusion, the Cu coating on surfaces of GFs can generally improve the interfacial bonding, mechanical properties and thermal properties of GFs(Cu)/Cu laminated composites. It provides an effective way to develop novel structural and functional materials for thermal management.

Achieving Isotropic Thermal Properties in Graphite Flake/cu Composites Through the Radial Structural Design of Reinforcement

Fabrication, mechanical and thermal properties of tungsten-copper coated graphite flakes reinforced copper matrix composites

Synergistic enhancing effect of tungsten-copper coated graphite flakes and aluminum nitride nanoparticles on microstructure, mechanical and thermal properties of copper matrix composites

High thermal conductivity of GF@Cu@Ni/Si/Al composites reinforced with Cu and Ni co-deposited graphite flakes

Fabrication of Cu/graphite film/Cu sandwich composites with ultrahigh thermal conductivity for thermal management applications

Effects of Zr-Cu Alloy Powder on Microstructure and Properties of Cu Matrix Composite with Highly-Aligned Flake Graphite

Synergistic effects of tungsten coating on the microstructure, thermophysical and mechanical properties of graphite flakes reinforced copper matrix composites

Fabrication, Mechanical and Thermal Properties of Copper Coated Graphite Films Reinforced Copper Matrix Laminated Composites Via Ultrasonic-Assisted Electroless Plating and Vacuum Hot-Pressing Sintering

Thermal Properties of Graphene/metal Composites with Aligned Graphene

Fabrication, Interface Characterization and Modeling of Oriented Graphite Flakes/Si/Al Composites for Thermal Management Applications

Sintering behavior and thermal conductivity of graphite flakes/uranium dioxide composites

Three Dimensional AlN Skeleton-Reinforced Highly Oriented Graphite Flake Composites with Excellent Mechanical and Thermophysical Properties

Anisotropic Thermal Conductivity and Associated Heat Transport Mechanism in Roll-to-roll Graphene Reinforced Copper Matrix Composites

Microstructure and properties of graphite nanoflakes/Cu matrix composites fabricated by pressureless sintering and subsequent thermo-mechanical treatment

Isotropic Porous Graphite Foam/epoxy Composites with Outstanding Heat Dissipation and Excellent Electromagnetic Interference Shielding Performances

Wide and Fine Alignment Control and Interface Modification for High-Performance Thermally Conductive Graphite/copper Composite

Achieving high thermal conductivity in CNTs@GF/Al laminates via a rapid and simple strategy

Enhancing the Mechanical and Thermophysical Properties of Highly Oriented Graphite Flake Composites by Formation of a Uniform Three Dimensional Tungsten Carbide Skeleton Reinforcement

High thermal and mechanical properties of carbon fiber network reinforced copper matrix composites achieved by configuration design and interface engineering

Enhanced thermal conductivity and isotropy of polymer composites by fabricating 3D network structure from carbon‐based materials

Preparation and properties of resin matrix composites reinforced by high thermal conductivity graphite films