Manipulating Horizontal Zn Deposition with Indium Salt Additive for Anode-Free Zn Batteries

Viktor Vanoppen,Erik J. Berg,Leiting Zhang,Xu Hou

DOI: https://doi.org/10.26434/chemrxiv-2024-p3j5n

2024-08-02

Abstract:Anode-free Zn batteries are gaining significant interest due to their reduced weight and simplified production compared to traditional Zn metal batteries. However, challenges such as zinc dendrite formation and parasitic reactions continue to impact their efficiency and cycle life. In this study, we present an effective strategy to form a zincophilic interphase in situ via indium co-deposition during cycling, using InCl3 as an electrolyte additive. We investigated the zinc plating/stripping processes with and without InCl3 using operando electrochemical quartz crystal microbalance with dissipation monitoring (EQCM-D). Structural changes from zinc deposition and dissolution were quantified using hydrodynamic spectroscopy (HS) and validated by ex-situ scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). Our findings demonstrate that the indium-containing electrolyte additive has triple functions: it induces oriented zinc deposition through pre-nucleation, suppresses hydrogen evolution reaction by forming an indium intermediate layer, and suppresses zinc hydroxide sulfate (ZHS) by consuming OH- with In2O3/InOOH formation. These advantages result in decreased overpotential and higher Coulombic efficiency, enhancing the design of highly reversible anode-free zinc batteries.

Chemistry

What problem does this paper attempt to address?

The paper mainly proposes solutions to the problems existing in anode-free zinc batteries. Anode-free zinc batteries have attracted widespread attention due to their advantages of reducing weight and simplifying the production process, but the formation of zinc dendrites and side reactions still severely affect the efficiency and cycle life of the batteries.

The research team added indium chloride (InCl₃) as an additive to the electrolyte and used the method of co-deposition of indium and zinc to form a zincophilic interphase in situ during the cycling process. This method can achieve directional deposition of zinc, inhibit the generation of hydrogen gas, and reduce the formation of zinc sulfate hydroxide compounds (ZHS). Specifically, the presence of indium has the following three functions:

1. **Inducing directional zinc deposition**: Promoting zinc deposition along specific directions (such as the (002) plane) through a pre-nucleation process.
2. **Inhibiting hydrogen gas generation reaction**: Forming an indium intermediate layer to inhibit the generation of hydrogen gas.
3. **Reducing ZHS formation**: Consuming the generated OH⁻ ions to form In₂O₃ or InOOH, thereby avoiding the production of ZHS.

These advantages collectively reduce the overpotential, improve the coulombic efficiency, and help design more reversible anode-free zinc batteries. Experimental results show that in the electrolyte containing 1 mM InCl₃, the zinc deposition/stripping process is more uniform and flat, achieving higher coulombic efficiency and better reversibility.

In summary, this paper aims to improve the performance of anode-free zinc batteries by controlling zinc deposition, with a focus on the important role of indium in this process.