Abstract:It is vital to explore sustainable and highly efficient catalysts for the oxygen reduction reaction (ORR) with increasing energy demand. Herein, a cobalt (Co) atom dispersed on an N-doped carbon nanosphere catalyst (denoted as ) was designed and constructed by a simple precursor-engineering method. The regulation of heteroatoms and Co metal atoms in precursors introduces more defects and thus reduces the degree of graphitization in the catalyst. The high N content of 5.23 at% in the catalyst provides abundant N sites to anchor metallic Co atoms, which further increases the defects for enhanced catalytic activity. The obtained with an ultralow loading of Co (only 0.041 wt %) exhibits an onset potential of 1.05 V, a limited-diffusion current density of 4.74 mA/cm<sup>2</sup>, and a half-wave potential of 0.79 V for the ORR under alkaline conditions, comparable to those of commercial Pt/C (1.06 V, 4.58 mA/cm<sup>2</sup>, and 0.81 V, respectively). Therefore, the synergistic effect of heteroatoms and Co metal atoms is beneficial for tuning the carbon matrix defects, which leads to the improvement of ORR activity. The Koutecky–Levich equation and rotating ring-disk electrode tests reveal a complete four-electron oxygen reduction pathway, impeding hydrogen peroxide generation. Moreover, nearly 93.8% of the current is retained for after 10 h stability testing without any morphological structural collapse. Meanwhile, it demonstrates superior tolerance to methanol. Our discovery opens a door to engineering the defects of carbon catalysts through introducing ultralow loading of non-noble metal atoms on substrates.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaem.0c03197?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaem.0c03197</a>.**Polarization curves of catalysts for temperature regulation; TEM and HAADF-STEM graphs; TGA curves of catalysts; XRD and Raman analysis of ECo-900; XPS C1s spectra of catalysts; additional cyclic voltammogram and LSV data; stability testing data; methanol resistance testing data; K–L plots and electron number; cycling performance of Zn-air equipped battery data; and element analysis results (<a class="ext-link" href="/doi/suppl/10.1021/acsaem.0c03197/suppl_file/ae0c03197_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Engineering Asymmetric Electronic Structure of Cobalt Coordination on CoN3S Active Sites for High Performance Oxygen Reduction Reaction

Engineering asymmetric electronic structure of cobalt coordination on CoN 3 S active sites for high performance oxygen reduction reaction

Engineering the morphology and electronic structure of atomic cobalt-nitrogen-carbon catalyst with highly accessible active sites for enhanced oxygen reduction

Asymmetric Coordination Regulating D‐orbital Spin‐electron Filling in Single‐atom Iron Catalyst for Efficient Oxygen Reduction

Engineering Asymmetric Fe Coordination Centers with Hydroxyl Adsorption for Efficient and Durable Oxygen Reduction Catalysis

CoN4 active sites in locally distorted carbon structure for efficient oxygen reduction reaction via regulating coordination environment

Enhancing Defects of N-Doped Carbon Nanospheres Via Ultralow Co Atom Loading Engineering for a High-Efficiency Oxygen Reduction Reaction

Cobalt Nanoparticles Embedded in N, S Co‐Doped Carbon Towards Oxygen Reduction Reaction Derived by in Situ Reducing Cobalt Sulfide

Engineering of Nitrogen Coordinated Single Cobalt Atom Moieties for Oxygen Electroreduction

Coordination Engineering of Defective Cobalt-Nitrogen-Carbon Electrocatalysts with Graphene Quantum Dots for Boosting Oxygen Reduction Reaction

Synergistically Enhanced Oxygen Reduction Electrocatalysis by Atomically Dispersed and Nanoscaled Co Species in Three-Dimensional Mesoporous Co, N-codoped Carbon Nanosheets Network

Dual Carbon-Hosted Co-N3 Enabling Unusual Reaction Pathway for Efficient Oxygen Reduction Reaction

Single Atomic Cobalt Electrocatalyst for Efficient Oxygen Reduction Reaction

Core-Shell ZIF-67@ZIF-8-derived multi-dimensional cobalt-nitrogen doped hierarchical carbon nanomaterial for efficient oxygen reduction reaction

Engineering the Electronic Structure of PtCo Sites Via Electron Injection to CoNC Boosts Acidic Oxygen Electroreduction

In situ modulating coordination fields of single-atom cobalt catalyst for enhanced oxygen reduction reaction

Experimental and Dft Studies of Oxygen Reduction Reaction Promoted by Binary Site Fe/Co-N-C Catalyst in Acid

Coordinatively Unsaturated Single Co Atoms Immobilized on C2N for Efficient Oxygen Reduction Reaction

Strong Electronic Metal-Support Interactions Enable the Increased Spin State of Co-N4 Active Sites and Performance for Acidic Oxygen Reduction Reaction

Atomically Dispersed Co 2 –N 6 and Fe–N 4 Costructures Boost Oxygen Reduction Reaction in Both Alkaline and Acidic Media

A highly efficient axial coordinated CoN5 electrocatalyst via pyrolysis-free strategy for alkaline polymer electrolyte fuel cells