Superior Pd-Rh Three-Way Catalyst: Modulating the Surface Composition by Introducing Ceria-Zirconia with Partial -Ce<sub>2</sub>Zr<sub>2</sub>O<sub>8</sub> Structure as Support
Xinyi Yin,Shanshan Li,Jie Deng,Yun Wang,Mengchen Li,Yi Zhao,Wei Wang,Jianli Wang,Yaoqiang Chen
DOI: https://doi.org/10.1021/acs.iecr.2c02319
2022-01-01
Industrial & Engineering Chemistry Research
Abstract:Surface segregation with Pd enrichment, diminishing the desired characteristics of the Rh species, remains as a key challenge for CZ (ceria-zirconia-based oxide)-supported Pd-Rh three-way catalyst under high-temperature treatment. Regulating the metal-support interactions by handling the characteristics of supports is an effective method to inhibit this deterioration phenomenon. As compared with traditional CZ, kappa CZ (partial kappa-Ce2Zr2O8 structure) with an adequate surface area interacts strongly with Pd due to its lower oxygen vacancies energy, which stabilizes the Pd species in the oxidation states and small sizes. Meanwhile, the relative Zr-rich surface of kappa CZ benefits the suppression of the formation of RhQ(x) caused by stronger electron transfer between Rh and CZ. Therefore, a strategically designed kappa CZ support was fabricated to tune the local composition of the Pd-Rh bimetal catalyst by the optimized interaction between Pd/Rh and kappa CZ. By XPS, CO FTIR and CO chemisorption tests, more highly reactive Pd delta+(delta > 2) species in smaller sizes could be maintained on kappa CZ (46.52%, 17.4 nm) comparing with that on CZ (37.38%, 23.1 nm) due to the stronger Pd-O-Ce/Zr bonds. Meanwhile, more Rh species in active sates (Rh-0) could be kept on kappa CZ (19.10%) than on CZ (13.11%) because of the decrease of Rh-O-Ce interfaces. As a result, the local composition of Pd-Rh/kappa CZ was optimized. Also the Pd-rich surface was avoided as compared with the Pd-Rh/CZ surface, and a greater proportion of active components (Rh-0 and Pd delta+) was exposed. Then, an advanced Pd-Rh/kappa CZ catalyst for TWC performance was designed, specifically, and after high thermal aging treatment, the T-50 and T-90 of the four pollutants (CO, NO, C3H8, and C3H6) were lower by more than 20 degrees C as compared to that for Pd-Rh/CZ.