Study on Microstructure of Cemented Paste Backfill with Initial Defects under Uniaxial Compression Failure

Yang Liu,Kang Zhao,Juncheng Zhong,Yun Zhou,Daotan Wen,Weiling Xiao

DOI: https://doi.org/10.1016/j.conbuildmat.2024.137528

IF: 7.4

2024-01-01

Construction and Building Materials

Abstract:In order to fully understand the micro and fine structural characteristics of the cemented paste backfill (CPB) with initial defects, this paper carries out uniaxial compression test on the CPB and real-time monitoring with DIC technology, analyses the crack extension and deformation characteristics on the surface of the specimen, carries out SEM test on the damaged specimen, binarizes the SEM images, and performs microscopic pore analysis on the processed binarized images using PCAS software. Then some parameters such as porosity, probability entropy, probability distribution index, fractal dimension, form factor, etc. of the specimens with different initial defects are discussed. The study shows that the damage form of CPB under uniaxial compression is mainly tensile damage, and gradually changes from tensile damage to shear damage when the specimen reaches the peak strength. The overall displacement and strain of each monitoring point on the specimen increases rapidly after entering the plastic deformation stage. There are many small microcracks and pores in the CPB, and there are a large number of aciculate ettringite and C-S-H gel hydration products, which are generated in the sample unevenly. With the addition of air-entraining agent (AEA), within a certain range, the number of pores inside the CPB increases. Many small pores also form large pores because of the connectivity between the pores, the porosity of the specimen increases, and the morphology and structure of the pores are relatively more regular. However, the direction of the pore development still does not have good directionality, and the initial defects become increasingly obvious.