Constructing a Multiple Covalent Interface and Isolating Disperion Structure in Silica/Rubber Nanocomposites with Excellent Dynamic Performance.
Junchi Zheng,Dongli Han,Suhe Zhao,Xin Ye,Yiqing Wang,Youping Wu,Dong Dong,Jun Liu,Xiaohui Wu,Liqun Zhang
DOI: https://doi.org/10.1021/acsami.8b02358
IF: 9.5
2018-01-01
ACS Applied Materials & Interfaces
Abstract:Realizing and manipulating a fine dispersion of silica nanoparticles (NPs) in the polymer matrix is always a great challenge. In this work, we firstly successfully synthesized N, N'-bis[3-(triethoxysilyl)propyl-isopropanol] -propane-1, 3-diamine (TSPD), which was a new interface modifier, aiming to promote the dispersion of silica NPs. Through the Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance analyses (NMR) and mass spectroscopy, we verified that the TSPD contains together six ethoxy groups at its two ends. Then, we used this TSPD to modify the pure silica NPs and this modified silica was abbreviated as D-MS, which is realized by the TGA examination, scanning electron microscopy (SEM) analyses and dynamic light scattering (DLS) results. It was clearly observed that D-MS NPs are connected to one another but are not conglutinated tightly, exhibiting a novel pre-dispersed structure with around 1-2 nm certain extent of inter-particle distance. Next, we fabricated the following four elastomer nanocomposites such as pure silica/natural rubber (NR) composite (PS-NR), D-MS/NR composite (DMS-NR), bis-(γ-triethoxysilylpropyl)-tetrasulfide (TESPT) modified silica/NR composite (TS-NR) and TESPT modified D-MS/NR composite (T&DMS-NR), and found that the Payne effect is the smallest for T&DMS-NR via the combination use of the D-MS and the traditional coupling agent TESPT, attributed to its best dispersion state evidenced by the TEM results. Moreover, by measuring a series of other important mechanical performances such as the stress-strain curve, the dynamic strain dependent of the loss factor and the heat build-up, the T&DMS-NR system greatly exceeds those of the three other rubber composites. In general, this new approach provides a good opportunity to prepare a silica/rubber composite with excellent properties in mechanics strength and dynamic behavior by tailoring the fine dispersion of NPs.